On the effects of stitching in CFRPs - I. Mode I delamination toughness

被引：227

作者：

Dransfield, KA

Jain, LK

Mai, YW ^{[1
]}

机构：

[1] Univ Sydney, Dept Mech & Mechatron Engn, Ctr Adv Mat Technol, Sydney, NSW 2006, Australia

[2] Cooperat Res Ctr Adv Composite Struct Ltd, Bankstown, NSW 2200, Australia

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 1998年 / 58卷 / 06期

关键词：

textile composites; fracture toughness; delamination; fibre bridging; resin transfer moulding (RTM);

D O I：

10.1016/S0266-3538(97)00229-7

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

Stitching advanced carbon-fibre composites in the thought-thickness direction enhances the interlaminar fracture toughness. The mode I delamination roughness of a carbon/epoxy composite, both unstitched and stitched, was experimentally determined by using double-cantilever beam specimens. Specimens with varying stitch density, thread diameter and thread type were studied. The steady-state toughnesses, G(IRs) Of unstitched and stitched specimens have been compared. The addition of stitching was found to create an improvement in toughness of up to 15 times. The energy-dissipating crack propagation processes were determined and critical parameters identified. In addition, experimental results were compared with theoretical predictions from a micromechanics-based model developed previously and good agreement was found. (C) 1998 Elsevier Science Ltd. All rights reserved.

引用

页码：815 / 827

页数：13

共 29 条

[1]

*ASTM, 1985, D225681 ASTM

[2]

*ASTM, 1985, D337975 ASTM

[3]

*ASTM, 1985, D321779 ASTM

[4] FRACTURE-BEHAVIOR IN STITCHED MULTIDIRECTIONAL COMPOSITES [J].

CHUNG, WC ;

JANG, BZ ;

CHANG, TC ;

HWANG, LR ;

WILCOX, RC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 112 :157-173

[5]

Cotterell B., 1996, FRACTURE MECH CEMENT

[6]

DOW MB, 1989, INT SAMPE TECH CONF, V21, P595

[7] IMPROVING THE DELAMINATION RESISTANCE OF CFRP BY STITCHING - A REVIEW [J].

DRANSFIELD, K ;

BAILLIE, C ;

MAI, YW .

COMPOSITES SCIENCE AND TECHNOLOGY, 1994, 50 (03) :305-317

[8]

DRANSFIELD K, 1995, P ICCM 10 C VANC AUG

[9]

DRANSFIELD KA, 1995, THESIS U SYDNEY

[10] COMPRESSION RESPONSE OF THICK LAYER COMPOSITE LAMINATES WITH THROUGH-THE-THICKNESS REINFORCEMENT [J].

FARLEY, GL ;

SMITH, BT ;

MAIDEN, J .

JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1992, 11 (07) :787-810

← 1 2 3 →