On the effects of stitching in CFRPs - I. Mode I delamination toughness

被引：227

作者：

Dransfield, KA

Jain, LK

Mai, YW ^{[1
]}

机构：

[1] Univ Sydney, Dept Mech & Mechatron Engn, Ctr Adv Mat Technol, Sydney, NSW 2006, Australia

[2] Cooperat Res Ctr Adv Composite Struct Ltd, Bankstown, NSW 2200, Australia

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 1998年 / 58卷 / 06期

关键词：

textile composites; fracture toughness; delamination; fibre bridging; resin transfer moulding (RTM);

D O I：

10.1016/S0266-3538(97)00229-7

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

Stitching advanced carbon-fibre composites in the thought-thickness direction enhances the interlaminar fracture toughness. The mode I delamination roughness of a carbon/epoxy composite, both unstitched and stitched, was experimentally determined by using double-cantilever beam specimens. Specimens with varying stitch density, thread diameter and thread type were studied. The steady-state toughnesses, G(IRs) Of unstitched and stitched specimens have been compared. The addition of stitching was found to create an improvement in toughness of up to 15 times. The energy-dissipating crack propagation processes were determined and critical parameters identified. In addition, experimental results were compared with theoretical predictions from a micromechanics-based model developed previously and good agreement was found. (C) 1998 Elsevier Science Ltd. All rights reserved.

引用

页码：815 / 827

页数：13

共 29 条

[21]

MORALES A, 1990, 22 INT SAMPE TECH C, P1217

[22]

MOSTOVOY S, 1967, J MATER, V2, P661

[23]

Ogo Y, 1987, THESIS U DELAWARE

[24]

PELSTRING RM, 1989, 34 INT SAMPE S MAY, P1519

[25]

SHARMA SK, 1994, P 9 TECHN C AM SOC C

[26]

Su K., 1989, ASTM STP, P279

[27]

TAI SW, 1988, COMPOSITES DESIGN, P11

[28] Failure of transversely stitched RTM lap joints [J].

Tong, L ;

Jain, LK ;

Leong, KH ;

Kelly, D ;

Herszberg, I .

COMPOSITES SCIENCE AND TECHNOLOGY, 1998, 58 (02) :221-227

[29]

WILKINS DJ, 1983, AGARD C P, V355

← 1 2 3 →