Hydrogen capacity of palladium-loaded carbon materials

Several samples of palladium-loaded single-wall carbon nanotubes and palladium-loaded MAXSORB activated carbon were prepared by means of the reaction of the raw carbon support with Pd-2(dba)(3)center dot CHCl3. When carbon nanotubes were used as the support, the palladium content in the samples reached 13-31 wt % and fine particles of 5-7 nm average size were obtained. In the case of the samples with MAXSORB as the support, the palladium content was higher (30-50 wt %) and the particle size larger (32-42 nm) than in the nanotube samples. At 1 atm and room temperature, the hydrogen capacity of the palladium-loaded samples exceeds 0.1 wt % and is much higher than the capacity of the raw carbon supports (less than 0.01 wt %). The maximum hydrogen capacity at 1 atm and room temperature was found to be 0.5 wt %. A maximum hydrogen capacity of 0.7 wt % was obtained at 90 bar in a palladium-loaded MAXSORB sample, while the capacities for the raw carbon nanotubes and MAXSORB at the same pressure were 0.21 and 0.42 wt %, respectively. At low pressure, it was observed that the H/Pd atomic ratios in the palladium-loaded samples were always higher than in the bulk Pd. The spillover effect is considered as a possible cause of the high H/Pd atomic ratios. On the other hand, the effect of the pressure increase on the spillover was observed to be very low at high pressure and room temperature.