Effect of carbon nanofiber reinforcement on mechanical properties of syntactic foam

被引：45

作者：

Zhang, Liying ^{[1
]}

Ma, J. ^{[1
]}

机构：

[1] Nanyang Technol Univ, Sch Mat Sci & Engn, Singapore 639798, Singapore

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 574卷

关键词：

Mechanical characterization; Composites; Failure; Fracture; FIBER REINFORCEMENT; FLEXURAL BEHAVIOR; FRACTURE; COMPOSITES;

D O I：

10.1016/j.msea.2013.03.028

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of carbon nanofiber (CNF) content on mechanical properties of syntactic foams was evaluated experimentally. Compression, flexural, and fracture toughness tests were performed to observe the mechanical behaviors of CNF reinforced syntactic foams (CNFRSFs). Results showed that no enhancement in compressive strength with addition of CNFs was observed. The flexural strength and fracture toughness increased with the increase in CNFs content. The decreasing trend occurred beyond 1.5 vol% of CNFs addition, which is ascribed to the agglomeration and clustering of CNFs. The toughening mechanisms, such as crack deflection, step structure, and debonding were proposed and the specific properties of CNFRSFs were also discussed in this paper. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：191 / 196

页数：6

共 24 条

[21] Specific properties and fracture toughness of syntactic foam: Effect of foam microstructures [J].

Wouterson, EM ;

Boey, FYC ;

Hu, X ;

Wong, SC .

COMPOSITES SCIENCE AND TECHNOLOGY, 2005, 65 (11-12) :1840-1850

[22] Effect of fiber reinforcement on the tensile, fracture and thermal properties of syntactic foam [J].

Wouterson, Erwin M. ;

Boey, Freddy Y. C. ;

Hu, Xiao ;

Wong, Shing-Chung .

POLYMER, 2007, 48 (11) :3183-3191

[23] Effect of coupling agent on mechanical properties of hollow carbon microsphere/phenolic resin syntactic foam [J].

Zhang, Liying ;

Ma, J. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2010, 70 (08) :1265-1271

[24] Processing and characterization of syntactic carbon foams containing hollow carbon microspheres [J].

Zhang, Liying ;

Ma, J. .

CARBON, 2009, 47 (06) :1451-1456

← 1 2 3 →