Effect of cold rolling reduction on secondary recrystallization of 3%Si-FE

被引：11

作者：

Arai, S ^{[1
]}

Ushigami, Y ^{[1
]}

Takahashi, N ^{[1
]}

机构：

[1] NIPPON STEEL CORP LTD,TECH DEV BUR,FUTTSU,CHIBA 293,JAPAN

来源：

GRAIN GROWTH IN POLYCRYSTALLINE MATERIALS II, PTS 1 AND 2 | 1996年 / 204-卷

关键词：

silicon steel; Goss texture; secondary recrystallization; cold rolling;

D O I：

10.4028/www.scientific.net/MSF.204-206.617

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of cold rolling reductions on secondary recrystallization of 3%Si-Fe was investigated. Secondary recrystallization structures were developed completely for all the specimens cold rolled in the reduction range from 50 to 95%. The average grain diameters of the secondaries were found to increase with the reduction increase. Three orientation components of {110}< 227 >, {110}< 001 >, and {110}< 112 > orientations developed depending on the cold rolling reductions. The main components were the {110}< 227 > orientation for 50 and 70% reductions, the sharp {110}< 001 > for a 88% reduction, and the {110}< 112 > for a 95% reduction.

引用

页码：617 / 622

页数：6

共 13 条

[1]

HAASE J, 1986, T JIM, V27, P563

[2]

MAY JE, 1958, T AM I MIN MET ENG, V212, P769

[3] EFFECT OF REDUCTION OF COLD-ROLLING ON SECONDARY RECRYSTALLIZATION OF GRAIN-ORIENTED ELECTRICAL STEEL PRODUCED BY SINGLE-STAGE COLD-ROLLING PROCESS [J].

NAKASHIMA, S ;

TAKASHIMA, K ;

HARASE, J .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (10) :1710-1716

[4]

NAKAYAMA T, 1993, THESIS KYOTO U

[5]

NARITA K, 1977, DENKI GAKKAISHI, V97, P460

[6] SEM STUDY OF ORIGIN OF GOSS TEXTURE IN FE-3-25SI [J].

PEASE, NC ;

JONES, DW ;

WISE, MHL ;

HUTCHINSON, WB .

METAL SCIENCE, 1981, 15 (05) :203-209

[7] PREDICTION OF SECONDARY RECRYSTALLIZATION TEXTURE IN FE-3-PERCENT SI BY 3-DIMENSIONAL TEXTURE ANALYSIS [J].

SHIMIZU, R ;

HARASE, J ;

DINGLEY, DJ .

ACTA METALLURGICA ET MATERIALIA, 1990, 38 (06) :973-978

[8]

SHIMIZU R, 1988, CURR ADV MAT P, V1, P1839

[9] EFFECT OF PRIMARY RECRYSTALLIZED TEXTURE ON BEHAVIOR OF SECONDARY RECRYSTALLIZATION IN 3 PERCENT SILICON STEEL [J].

SHINOZAKI, M ;

MATOBA, I ;

KAN, T ;

GOTOH, T .

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1978, 19 (02) :85-91

[10]

TAKAHASHI N, INPRESS P 2 INT C GR

← 1 2 →