The effect of post weld heat treatment on the properties of 6061 friction stir welded joints

被引：116

作者：

Krishnan, KN ^{[1
]}

机构：

[1] Univ Adelaide, Dept Mech Engn, CRC Welded Struct, Adelaide, SA 5005, Australia

来源：

JOURNAL OF MATERIALS SCIENCE | 2002年 / 37卷 / 03期

关键词：

D O I：

10.1023/A:1013701104029

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Post weld heat treatment (PWHT) of Friction Stir Welds (FSW) was carried out at solutioninsing temperatures of 520, 540, and 560degreesC followed by ageing at 175degreesC or 200degreesC. It was found that the weld (stir) region exhibited very coarse grains after the PWHT. The hardness was found to be uniform across the weldment after the PWHT. The samples failed after PWHT during root bend test. Heat treatments to reduce the grain size did not reduce the brittleness of the welds. The brittleness was attributed to the presence of precipitate free zones adjacent to the grain boundaries and the equiaxed structure of the weldment microstructure and the failure was due to a ductile intergranular fracture mechanism. (C) 2002 Kluwer Academic Publishers.

引用

页码：473 / 480

页数：8

共 17 条

[1]

*ASM, 1990, ASM MET HDB, V2

[2]

Backlund J., 1998, P NALCO 7 CAMBR 16 A, P171

[3] DISLOCATION-STRUCTURES CAUSED BY PLASTIC-DEFORMATIONS IN AN AGED AL-MG-SI ALLOY [J].

BANIZS, K .

MATERIALS SCIENCE AND ENGINEERING, 1979, 41 (01) :17-24

[4] THE EFFECT OF DISPERSOIDS ON THE MICROMECHANISMS OF CRACK EXTENSION IN AL-MG-SI ALLOYS [J].

BLIND, JA ;

MARTIN, JW .

JOURNAL OF MATERIALS SCIENCE, 1983, 18 (04) :1224-1234

[5] THE EFFECT OF DISPERSOIDS ON THE DUCTILE FRACTURE-TOUGHNESS OF AL-MG-SI ALLOYS [J].

BLIND, JA ;

MARTIN, JW .

MATERIALS SCIENCE AND ENGINEERING, 1983, 57 (01) :49-54

[6] INFLUENCE OF MN ADDITIONS ON DEFORMATION-BEHAVIOR OF AN AL-MG-SI ALLOY [J].

DOWLING, JM ;

MARTIN, JW .

ACTA METALLURGICA, 1976, 24 (12) :1147-1153

[7]

EDWARDS L, 1986, MATER SCI TECH SER, V2, P823, DOI 10.1179/026708386790219714

[8] INTERGRANULAR FRACTURE OF AL-MG-SI ALLOYS [J].

EVENSEN, JD ;

RYUM, N ;

EMBURY, JD .

MATERIALS SCIENCE AND ENGINEERING, 1975, 18 (02) :221-229

[9]

KRISHNAN KN, 2001, P INT C WELD NEW DEL

[10] Microstructural aspects of the friction-stir welding of 6061-T6 aluminum [J].

Liu, G ;

Murr, LE ;

Niou, CS ;

McClure, JC ;

Vega, FR .

SCRIPTA MATERIALIA, 1997, 37 (03) :355-361

← 1 2 →