Mechanical behavior of various nanoparticle filled composites at low-velocity impact

被引:131
作者
Lin, Jin-Chein [1 ]
Chang, L. C. [1 ]
Nien, M. H. [1 ]
Ho, H. L. [1 ]
机构
[1] No Taiwan Inst Sci & Technol, Dept Mech Engn, Taipei 11202, Taiwan
关键词
low-velocity impact; nanocomposites; mechanical behavior; reinforced fillers; exfoliation; homogeneity;
D O I
10.1016/j.compstruct.2005.03.006
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
Low-velocity impact tests were performed on the various nanoparticle filled composites using a falling mass impact tester. The mechanical behavior and fracture morphology of two synthesized nanocomposites were investigates using polymer resin as the matrix and two types of filler contents as the reinforcing elements. To study the effect of exfoliated natioparticles on the properties of epoxy matrix, titanium dioxide and cloisite (R) 30B nanopowder were prepared with the filler content varied from 2 to 10 vol%. Significant improvement in mechanical properties of modulus was obtained when particle exfoliation and dispersion homogeneity were achieved. The impact energy and the corresponding initial velocity at 2.1, 5.2 and 8.1 m/s for both reinforced nanocomposites are conducted and found to have the linear relationship with both impact results. The experimental results imply that the degree of exfoliation may exhibit a maximum with respect to tensile strength, but show a minimum with respective to impact strength. It is found that the tensile strength, loss modulus, impact strength and dynamic thermal rheology of nanocomposites are extensively affected by the geometry, temperature, volume and type of filler content, and homogeneity of the nanoparticles. (c) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码:30 / 36
页数:7
相关论文
共 21 条
[11]   CORRELATION BETWEEN IMPACT STRENGTH AND DYNAMIC MODULUS FOR PLASTICS [J].
LIANG, X ;
MCNALLY, G ;
SPEDDING, PL ;
CRAWFORD, RJ .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1990, 9 (12) :1478-1480
[12]   INSTRUMENTED DART IMPACT EVALUATION OF LINEAR LOW-DENSITY POLYETHYLENE AT CONTROLLED IMPACT ENERGY [J].
LIU, TM ;
BAKER, WE .
POLYMER ENGINEERING AND SCIENCE, 1991, 31 (10) :753-763
[13]  
RILEY AM, 1990, PLAST RUB PROC APPL, V14, P85
[14]  
Roy R., 1987, CERAM MICROSTRUCT, V86, P25, DOI [10.1007/978-1-4613-1933-7_3, DOI 10.1007/978-1-4613-1933-7_3]
[15]   Mechanical behavior of a ductile polyamide 12 during impact [J].
Schang, O ;
Billon, N ;
Muracciole, JM ;
Fernagut, F .
POLYMER ENGINEERING AND SCIENCE, 1996, 36 (04) :541-550
[16]   SHEAR DEFORMATION UNDER IMPACT CONDITIONS [J].
SJOERDSMA, SD ;
BOYENS, JPH ;
MOOIJ, JJ .
POLYMER ENGINEERING AND SCIENCE, 1985, 25 (04) :250-255
[17]   SYNTHESIS OF NYLON 6-CLAY HYBRID [J].
USUKI, A ;
KOJIMA, Y ;
KAWASUMI, M ;
OKADA, A ;
FUKUSHIMA, Y ;
KURAUCHI, T ;
KAMIGAITO, O .
JOURNAL OF MATERIALS RESEARCH, 1993, 8 (05) :1179-1184
[18]   IMPACT STRENGTH AND MECHANICAL LOSSES IN THERMOPLASTICS [J].
VINCENT, PI .
POLYMER, 1974, 15 (02) :111-116
[19]  
Wang Q., 1997, TRIBOL INT, V30, P193
[20]  
WETZEL B, 2001, P 13 ICCM BEIJ