Hydrogen storage properties in Ti catalyzed Li-N-H system

被引:100
作者
Ichikawa, T
Hanada, N
Isobe, S
Leng, HY
Fujii, H
机构
[1] Hiroshima Univ, N BARD, Ctr Mat Sci, Higashihiroshima 7398526, Japan
[2] Hiroshima Univ, ADSM, Dept Quantum Matter, Higashihiroshima 7398530, Japan
关键词
hydrogen storage materials; nanostructures; gas-solid reactions; high-energy ball milling; thermal analysis;
D O I
10.1016/j.jallcom.2004.11.110
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The Li-N-H system expressed by LiNH2 + LiH <-> Li2NH + H-2 can be expected as a promising candidate for the hydrogen storage materials because of possessing a large amount of reversible hydrogen (6.5 wt.%), a satisfactorily fast kinetics and a relatively small enthalpy change. In this work, we investigated the hydrogen storage properties of the Li-N-H system from three different points of view. Firstly, we claim that the ball milled 1: 1 mixture of lithium amide (LiNH2) and lithium hydride (LiH) containing a small amount (I mol %) of titanium chloride (TiCl3) shows superior hydrogen storage properties; a large amount of H-2 gas desorbs in the temperature range from 150 to 250 degrees C at a heating rate of 5 degrees C/n-dn and it reveals an excellent reversibility. Secondly, we clarify that the above hydrogen desorption reaction is composed of two kinds of elementary reactions: The one is that 2LiNH(2) decomposes to Li2NH and emits ammonia (NH3). The other is that the emitted NH3 reacts with LiH and transforms into LiNH2 and H-2, indicating that NH3 plays an important role on this H-2 desorption reaction. Finally, we examined the reaction of LiH and LiOH to clarify the influence of exposing the product to air. This is because due to the fact that LiOH is easily produced by exposing LiH and LiNH2 to air. The reaction between LiH and LiOH indicated better kinetics but worse durability and an extra H2 desorption due to transforming into Li2O. (c) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码:435 / 438
页数:4
相关论文
共 12 条
[1]   Desorption of LiAlH4 with Ti- and V-based additives [J].
Blanchard, D ;
Brinks, HW ;
Hauback, BC ;
Norby, P .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2004, 108 (1-2) :54-59
[2]   Interaction of hydrogen with metal nitrides and imides [J].
Chen, P ;
Xiong, ZT ;
Luo, JZ ;
Lin, JY ;
Tan, KL .
NATURE, 2002, 420 (6913) :302-304
[3]  
CHEN P, 2003, J PHYS CHEM B, V420, P5135
[4]  
Dafert F.W., 1910, MONATSH CHEM, V31, P981
[5]   H2 storage in Li3N.: Temperature-programmed hydrogenation and dehydrogenation [J].
Hu, YH ;
Ruckenstein, E .
INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2003, 42 (21) :5135-5139
[6]   Mechanism of novel reaction from LiNH2 and LiH to Li2NH and H2 as a promising hydrogen storage system [J].
Ichikawa, T ;
Hanada, N ;
Isobe, S ;
Leng, HY ;
Fujii, H .
JOURNAL OF PHYSICAL CHEMISTRY B, 2004, 108 (23) :7887-7892
[7]   Lithium nitride for reversible hydrogen storage [J].
Ichikawa, T ;
Isobe, S ;
Hanada, N ;
Fujii, H .
JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 365 (1-2) :271-276
[8]  
LENG HY, UNPUB J PHYS CHEM A
[9]  
LENG HY, UNPUB J PHYS CHEM B
[10]   Li-N based hydrogen storage materials [J].
Nakamori, Y ;
Orimo, S .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2004, 108 (1-2) :48-50