Preparation and characterization of electrospun fibers of Nylon 11

被引：54

作者：

Dhanalakshmi, M. ^{[1
]}

Jog, J. P. ^{[1
]}

机构：

[1] Natl Chem Lab, Polymer Sci & Engn Div, Pune 411008, Maharashtra, India

来源：

EXPRESS POLYMER LETTERS | 2008年 / 2卷 / 08期

关键词：

nanomaterials; biocompatible polymers; electrospinning; Nylon; 11;

D O I：

10.3144/expresspolymlett.2008.65

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Nylon 11 nanofibers mats were successfully prepared by electrospinning process from formic acid solution. The scanning electron microscopy (SEM) images showed that nanofibers with uniform diameter were produced when the polymer concentration was 10% w/v, whereas ribbons were formed at a higher concentration. The crystalline structure of the nanofibers mats was investigated using X-ray diffraction (XRD) and it was found that the nanofibers mats crystallized in gamma form. The melt crystallized as well as solution casted films however exhibited a form. The thermal properties of these samples were studied using differential scanning calorimetry (DSC) and it was observed that electrospun fibers showed higher crystallinity than the melt-crystallized samples. However, the crystallinity of electrospun fibers was lower than the solution-crystallized sample.

引用

页码：540 / 545

页数：6

共 35 条

[1] New solvent for polyamides and its application to the electrospinning of polyamides 11 and 12 [J].

Behler, Kris ;

Havel, Mickael ;

Gogotsi, Yury .

POLYMER, 2007, 48 (22) :6617-6621

[2]

Bergshoef MM, 1999, ADV MATER, V11, P1362, DOI 10.1002/(SICI)1521-4095(199911)11:16<1362::AID-ADMA1362>3.0.CO

[3]

2-X

[4] Electrospun chitosan-based nanofibers and their cellular compatibility [J].

Bhattarai, N ;

Edmondson, D ;

Veiseh, O ;

Matsen, FA ;

Zhang, MQ .

BIOMATERIALS, 2005, 26 (31) :6176-6184

[5]

Buschle-Diller G, 2006, MODIFIED FIBERS WITH MEDICAL AND SPECIALTY APPLICATIONS, P67

[6] Mineralization of hydroxyapatite in electrospun nanofibrous poly(L-lactic acid) scaffolds [J].

Chen, Jinglu ;

Chu, Benjamin ;

Hsiao, Benjamin S. .

JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A, 2006, 79A (02) :307-317

[7] Processing and characterization of electrospun poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) nanofibrous membranes [J].

Cheng, Mei-Ling ;

Lin, Chih-Chung ;

Su, Hsiao-Lang ;

Chen, Po-Ya ;

Sun, Yi-Ming .

POLYMER, 2008, 49 (02) :546-553

[8] Electrospun nanofibers: Internal structure and intrinsic orientation [J].

Dersch, R ;

Liu, TQ ;

Schaper, AK ;

Greiner, A ;

Wendorff, JH .

JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2003, 41 (04) :545-553

[9] A nanofibrous composite membrane of PLGA-chitosan/PVA prepared by electrospinning [J].

Duan, Bin ;

Yuan, Xiaoyan ;

Zhu, Yi ;

Zhang, Yuanyuan ;

Li, Xiulan ;

Zhang, Yang ;

Yao, Kangde .

EUROPEAN POLYMER JOURNAL, 2006, 42 (09) :2013-2022

[10] Crystallization of Nylon 11 under compressive high strain rates [J].

Fernandez, JO ;

Swallowe, GM ;

Lee, SF .

JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 80 (11) :2031-2046

← 1 2 3 4 →