Transport properties and magnetic behavior in the polycrystalline lanthanum-deficient manganate perovskites (approximate to La1-xMnO3)

被引:14
作者
Ferris, V
Goglio, G
Brohan, L
Joubert, O
Molinie, P
Ganne, M
Dordor, P
机构
[1] UNIV NANTES,LAB CHIM SOLIDES,INST MAT NANTES,CNRS,UMR 110,F-44072 NANTES 03,FRANCE
[2] UNIV BORDEAUX 1,INST CHIM MAT CONDENSEE BORDEAUX,UPR 9048,F-33600 PESSAC,FRANCE
关键词
oxides; magnetic materials; electrical properties; magnetic properties;
D O I
10.1016/S0025-5408(97)00044-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The rhombohedral lanthanum manganates approximate to La1-xMnO3 (x = 0.0, 0.05, 0.1) were prepared by a soft chemistry route to test first as catalysts. These three weak ferromagnets exhibit a structural transition at T-t slightly below T-c. approximate to La0.9MnO3 undergoes a group-subgroup R (3) over bar c <---->, R3c transition most likely of second order. approximate to LaMnO3 does not show any insulator-to-metal transition, but does show a semiconductor-semiconductor at T-t similar to 130 K. Analysis of the transport data (conductivity and thermopower) indicates hopping of polarons at both low and high temperature. An effective magnetic moment of 3.50 mu(B)/Mn is deduced from the spontaneous magnetization value at 5 K. The slight difference from the spin-only value (3.67 mu B) is assigned to a spin-canting effect which is reflected in the divergence of the FC and ZFC susceptibility curves at low fields (H less than or equal to 10(-2) T) and low temperature. Compared with recent results on thin films, the compositions x = 0.05, 0.1 are expected to show magnetoresistive effects as well as a semiconductor-to-metal transition. If it is verified on bulk samples which all contain a similar Mn4+ content of 35%, the structural transition at T-t could be considered as magnetically driven. (C) 1997 Elsevier Science Ltd.