Structure and magnetic properties of Co nanoclusters fabricated by ion beam synthesis in SiO2 films

Co nanoparticles fabricated by ion beam synthesis in SiO2 films were investigated with transmission electron microscopy and superconducting quantum interference device technique. Variation of the thermal treatment enables the formation of Co nanoclusters of different sizes ranging from 2 to 40 nm. Small nanoclusters of about 2-3 nm are amorphous, whereas clusters above 7 nm show the configuration of cubic Co nanocrystals. Measurements of magnetisation at temperatures between 2 K and 360 K reveal superparamagnetic behaviour for the small nanoclusters up to 3 nm and ferromagnetism for clusters above 7 nm.