Synthesis of well-defined copper nanocubes by a one-pot solution process

被引：117

作者：

Wang, Yihai ^{[1
]}

Chen, Penglei ^{[1
]}

Liu, Minghua ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Chem, CAS Key Lab Colloid & Interface Sci, BNLMS, Beijing 100080, Peoples R China

来源：

NANOTECHNOLOGY | 2006年 / 17卷 / 24期

关键词：

D O I：

10.1088/0957-4484/17/24/016

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A simple one-pot solution-phase method was developed to synthesize well-defined copper nanocubes with an edge length in the range of 100 +/- 25 nm. Copper nanocubes were produced by using ascorbic acid as a reducing agent and poly( vinylpyrrolidone) (PVP) as a capping agent. X-ray diffraction (XRD), UV-vis spectroscopy (UV-vis), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) as well as selected-area electron diffraction (SAED) were used to characterize the resulting nanoparticles. The influence of concentration, temperature and additives on the formation of Cu nanoparticles was investigated. Some nano-polyhedra and nanospheres were also fabricated. Shape-controlled synthesis of copper nanoparticles was partially achieved.

引用

页码：6000 / 6006

页数：7

共 61 条

[51]

Toimil-Molares ME, 2001, ADV MATER, V13, P62, DOI 10.1002/1521-4095(200101)13:1<62::AID-ADMA62>3.0.CO

[52]

2-7

[53]

TSUCHIDA E, 1973, MAKROMOL CHEM, V164, P203

[54] Highly polarized photoluminescence and photodetection from single indium phosphide nanowires [J].