3D long fiber-reinforced syntactic foam based on hollow polymeric microspheres

被引:37
作者
Huang, YJ [1 ]
Vaikhanski, L [1 ]
Nutt, SR [1 ]
机构
[1] Univ So Calif, McGill Composites Ctr, Dept Mat Sci, Los Angeles, CA 90089 USA
关键词
aramid fibre; carbon fibre; foams; mechanical properities;
D O I
10.1016/j.compositesa.2005.02.014
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Composite syntactic foams comprised of amino microspheres reinforced with chopped fibers were fabricated using a phenolic resin binder. Compressive, shear, and tensile strength and moduli were measured in directions parallel and perpendicular to the preferred fiber orientation. The results showed substantial increases in strength and modulus compared with the unreinforced (neat) foam when measured parallel to the preferred fiber orientation. When loaded perpendicular to the dominant fiber orientation, properties were enhanced 30-40%, but when load was applied parallel to the dominant fiber orientation, the compression strength of the composite foam increased by a factor of up to 2; the tensile strength and modulus increased by a factor of up to 7 and 8, respectively, and the shear strength and modulus increased by a factor of up to 3.3 and 2.3, respectively. The fibers were more effective in enhancing the strength of syntactic foams when loads were applied parallel to the dominant fiber orientation. (c) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码:488 / 496
页数:9
相关论文
共 24 条
[1]  
Agarwal B.D., 1990, ANAL PERFORMANCE FIB, V2nd ed., P449
[2]  
AHMAD M, 2004, WPC 2004 C VIENN AUS
[3]  
*AS PAC CORP, 2003, TECH INF
[4]  
*BALT CORP, 2003, TECHN INF
[5]   Reactive microspheres as active fillers for epoxy resins [J].
Carfagna, C ;
Ambrogi, V ;
Cicala, G ;
Pollicino, A ;
Recca, A ;
Costa, G .
JOURNAL OF APPLIED POLYMER SCIENCE, 2004, 93 (05) :2031-2044
[6]   MECHANISM OF REINFORCEMENT OF POLYURETHANE FOAM BY HIGH-MODULUS CHOPPED FIBERS [J].
COTGREAVE, TC ;
SHORTALL, JB .
JOURNAL OF MATERIALS SCIENCE, 1977, 12 (04) :708-717
[7]  
*DUP CO, 2003, TECHN INF
[8]  
*EXP INC, 2003, EXP MICR TECHN INF
[9]   Compressive fracture features of syntactic foams-microscopic examination [J].
Gupta, N ;
Woldesenbet, E ;
Kishore .
JOURNAL OF MATERIALS SCIENCE, 2002, 37 (15) :3199-3209
[10]   Response of syntactic foam core sandwich structured composites to three-point bending [J].
Gupta, N ;
Woldesenbet, E ;
Kishore ;
Sankaran, S .
JOURNAL OF SANDWICH STRUCTURES & MATERIALS, 2002, 4 (03) :249-272