Study of the wear behavior and adhesion of diamond films deposited on steel substrates by use of a Cr-N interlayer

被引：39

作者：

Glozman, O

Halperin, G

Etsion, I

Berner, A

Shectman, D

Lee, GH

Hoffman, A ^{[1
]}

机构：

[1] Technion Israel Inst Technol, Dept Chem, IL-32000 Haifa, Israel

[2] Technion Israel Inst Technol, Wolfson Ctr Interfaces Sci, IL-32000 Haifa, Israel

[3] Technion Israel Inst Technol, Dept Mech Engn, IL-32000 Haifa, Israel

[4] Technion Israel Inst Technol, Dept Mat Engn, IL-32000 Haifa, Israel

[5] KIMM, Kyung Nam, South Korea

[6] Technion Israel Inst Technol, Inst Solid State, IL-32000 Haifa, Israel

来源：

关键词：

adhesion strength; diamond film; interface; tribology;

D O I：

10.1016/S0925-9635(98)00321-5

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In the present work, we report on the wear behavior and adhesion of diamond films deposited on steel coated by a Cr-N interlayer. The wear behavior of the diamond films was studied under fretting conditions. Fretting was used as a typical wear process occurring during vibration and friction. Wear grooves obtained after the fretting test under different loads and for different numbers of cycles were studied by profilometry, high-resolution scanning electron microscopy and electron probe microbeam analysis. The adhesion of the deposited diamond films was measured by using scratch and indentation tests. The fracture behavior of the diamond film/nitrided chromium interlayer complex under different conditions was studied and correlated to the interlayer nitridation conditions. (C) 1999 Elsevier Science S.A. All rights reserved.