Controlled interconversion of semiconducting and metallic forms of polyaniline nanofibers

被引:54
作者
Sarno, DM
Manohar, SK
MacDiarmid, AG
机构
[1] Univ Penn, Dept Chem, Philadelphia, PA 19104 USA
[2] Univ Texas, Dept Chem, Alan G MacDiarmid Lab Tech Innovat, Richardson, TX 75083 USA
关键词
polyaniline; nanofibers; doping; scanning electron microscopy;
D O I
10.1016/j.synthmet.2004.09.038
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Self-assembled polyaniline nanotibers doped with 2-acrylamido-2-methyl-1-propanesulfonic acid were prepared by oxidative polymerization of aniline in the presence of a nonionic surfactant. These nanofibers were dedoped to the semiconducting emeraldine base and then redoped to the metallic emeraldine hydrochloride. It was possible to introduce a different dopant anion from that used in the initial synthesis with no significant changes in fiber morphology or diameter, as observed by scanning electron microscopy (SEM). The method of sample preparation for SEM significantly affected the observed morphology. Deposition from aqueous dispersions resulted primarily in nanofibers that ranged in diameter from 28 to 82 nm (average: 56 nm), whereas drying to solid powder resulted in a less fibrous material. UV-vis-NIR absorbance spectroscopy indicated that the electronic structure of the emeraldine base nanofibers was identical to bulk emeraldine base obtained by conventional synthesis. Estimates from X-ray diffraction data suggested that the fractional crystallinity of emeraldine hydrochloride nanofibers did not differ significantly from the bulk powder. (C) 2004 Published by Elsevier B.V.
引用
收藏
页码:237 / 243
页数:7
相关论文
共 25 条
[1]  
[Anonymous], 1999, NAN REV MAK VIS R D
[2]   Controlled polymerization of aniline at sub-zero temperatures [J].
Beadle, PM ;
Nicolau, YF ;
Banka, E ;
Rannou, P ;
Djurado, D .
SYNTHETIC METALS, 1998, 95 (01) :29-45
[3]   COUNTERION INDUCED PROCESSIBILITY OF CONDUCTING POLYANILINE AND OF CONDUCTING POLYBLENDS OF POLYANILINE IN BULK POLYMERS [J].
CAO, Y ;
SMITH, P ;
HEEGER, AJ .
SYNTHETIC METALS, 1992, 48 (01) :91-97
[4]   POLYANILINE - PROTONIC ACID DOPING OF THE EMERALDINE FORM TO THE METALLIC REGIME [J].
CHIANG, JC ;
MACDIARMID, AG .
SYNTHETIC METALS, 1986, 13 (1-3) :193-205
[5]   Surface and precipitation polymerization of aniline [J].
Fedorova, S ;
Stejskal, J .
LANGMUIR, 2002, 18 (14) :5630-5632
[6]   A general chemical route to polyaniline nanofibers [J].
Huang, JX ;
Kaner, RB .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2004, 126 (03) :851-855
[7]   Selective deposition of films of polypyrrole, polyaniline and nickel on hydrophobic/hydrophilic patterned surfaces and applications [J].
Huang, Z ;
Wang, PC ;
Feng, J ;
MacDiarmid, AG ;
Xia, YN ;
Whitesides, GM .
SYNTHETIC METALS, 1997, 85 (1-3) :1375-1376
[8]   The influence of 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPSA) additive concentration and stretch orientation on electronic transport in AMPSA-modified polyaniline films prepared from an acid solvent mixture [J].
Hundley, MF ;
Adams, PN ;
Mattes, BR .
SYNTHETIC METALS, 2002, 129 (03) :291-297
[9]   Facile preparation of optically active polyanilines via the in situ chemical oxidative polymerisation of aniline [J].
Kane-Maguire, LAP ;
MacDiarmid, AG ;
Norris, ID ;
Wallace, GG ;
Zheng, WG .
SYNTHETIC METALS, 1999, 106 (03) :171-176
[10]  
KUMAR A, 2003, UNPUB