The electrochromic behavior of nickel oxide films sprayed at different preparative conditions

Nickel oxide films have been prepared onto transparent conducting-coated glass at different substrate temperatures using spray pyrolysis technique. Electrochromic characterizations of the prepared films have been studied by cycling between their coloured and bleached states using a three-electrode cell containing 1 M KOH electrolyte. The influence of substrate temperature as well as film thickness on the electrochromic (EC) performance has been investigated. The substrate temperature (T-sub), film thickness, and the colouration and bleaching potentials have been optimized as 275 degrees C, 140 nm, +0.7 and -1.0 V, respectively. With optimized coating and working parameters, the results yielded transmission solar modulation Delta T-S=0.35, visible modulation Delta T-v=0.51, injected charge-14 mC and colouration efficiency eta=44 cm(2)/C. In addition to the nominal bleaching state, a full bleaching state is newly assigned leading to higher optical modulation of 0.45 and 0.63 for Delta T-S and Delta T-v, respectively. An adequate potential pulse shape is suggested for operating the device. Different from some reported results, switching time measurements showed that colouration is faster than bleaching which may obscure different redox mechanisms of EC colouration. Infrared reflectance spectroscopy showed evidently the significance of water in the EC process. The results showed clear consistency with the view that a transparent film of Ni(OH)(2) is made absorbing through transformation to coloured NiOOH. Discussion of the results supports the colouration mechanism of double extraction of proton and electron. (c) 2004 Elsevier B.V. All rights reserved.