Organic/inorganic imide nanocomposites from aminophenylsilsesquioxanes

被引:201
作者
Choi, JW
Tamaki, R
Kim, SG
Laine, RM [1 ]
机构
[1] Univ Michigan, Ctr Macromol Sci & Engn, Ann Arbor, MI 48109 USA
[2] Univ Michigan, Dept Mat Sci & Engn, Ann Arbor, MI 48109 USA
关键词
D O I
10.1021/cm030286h
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
We present here part of an ongoing study on structure -processing-property relationships in cubic silsesquioxane (cube) nanocomposites. Here, we focus on imide nanocomposites prepared from octaaminophenylsilsesquioxane (OAPS) as a model nanobuilding block for rigid, high-temperature hybrid nanocomposite materials. OAPS units are linked NH2 vertex to NH2 vertex by reaction with various dianhydrides to form three-dimensional nanocomposites. The architecture of the organic tethers between vertices can be manipulated to optimize processability, rigidity, and thermomechanical properties. Studies were initiated using an extreme tether structure with zero flexibility prepared by solvent casting and then curing mixtures of OAPS with pyromellitic dianhydride (PMDA) at 330 degreesC. The resulting materials are extremely brittle, making thermomechanical property measurements quite difficult. Tether rigidity, length, and cross-link densities were then modified using reactions of OAPS with oxydiphthalic anhydride (ODPA) and diluting with oxydianiline (ODA) to adjust nanocomposite stiffness. FTIR and DMA of the OAPS/ODPA/ODA nanocomposites suggest that cure temperatures of >500 degreesC are necessary for optimal imidization. However, increasing the cross-link density alone by increasing OAPS loading without curing at high temperatures also significantly improves thermomechanical stabilities. DMA, TGA, and nanoindentation measurements show that macroscopic relaxation is eliminated completely at OAPS loadings of >60 mol % providing 5% mass loss at temperatures >570 degreesC and compressive moduli of approximate to3.8 GPa.
引用
收藏
页码:3365 / 3375
页数:11
相关论文
共 77 条
[61]   Processing vapour-deposited polyimide [J].
Tsai, FY ;
Alfonso, EL ;
Harding, DR ;
Chen, SH .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2001, 34 (20) :3011-3018
[62]   Low dielectric polyimide/poly(silsesquioxane)-like nanocomposite material [J].
Tsai, MH ;
Whang, WT .
POLYMER, 2001, 42 (09) :4197-4207
[63]   Dynamic mechanical properties of polyimide/poly(silsesquioxane)-like hybrid films [J].
Tsai, MH ;
Whang, WT .
JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 81 (10) :2500-2516
[64]   Polymer/layered silicate nanocomposites as high performance ablative materials [J].
Vaia, RA ;
Price, G ;
Ruth, PN ;
Nguyen, HT ;
Lichtenhan, J .
APPLIED CLAY SCIENCE, 1999, 15 (1-2) :67-92
[65]   STRUCTURAL EFFECTS ON THE TRANSPORT OF WATER IN POLYIMIDES [J].
VANALSTEN, JG ;
COBURN, JC .
MACROMOLECULES, 1994, 27 (14) :3746-3752
[66]   Polymeric silsesquioxanes: degree-of-intramolecular-condensation measured by mass spectrometry [J].
Wallace, WE ;
Guttman, CM ;
Antonucci, JM .
POLYMER, 2000, 41 (06) :2219-2226
[67]  
Wirnsberger G, 2000, ADV MATER, V12, P1450, DOI 10.1002/1521-4095(200010)12:19<1450::AID-ADMA1450>3.0.CO
[68]  
2-4
[69]  
Wu KH, 2001, J APPL POLYM SCI, V79, P965, DOI 10.1002/1097-4628(20010207)79:6<965::AID-APP20>3.3.CO
[70]  
2-7