Quantification of the interface strength between (Ti,Zr)N coatings and high speed steel

被引：7

作者：

Rother, B ^{[1
]}

Donohue, LA ^{[1
]}

Kappl, H ^{[1
]}

机构：

[1] SHEFFIELD HALLAM UNIV,MAT RES INST,SHEFFIELD S1 1WB,S YORKSHIRE,ENGLAND

来源：

SURFACE & COATINGS TECHNOLOGY | 1996年 / 82卷 / 03期

关键词：

adhesion; depth-sensing indentation measurements; PVD coatings; (Ti; Zr)N; wet cleaning;

D O I：

10.1016/0257-8972(95)02667-3

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The interface strength of physical vapour deposited (TiZr)N coatings was determined by qualitative evaluation of the spallation patterns around Rockwell C indents as well as by differential load feed analysis of depth-sensing indentation measurements. Varying values of interface strength were produced by different wet cleaning procedures of the high speed steel samples prior to magnetron sputtering. The results of both evaluation techniques were comparable. The highest interface strength was determined for electrochemically enhanced wet cleaning with acidic neutralization.

引用

页码：214 / 217

页数：4

共 6 条

[1]

DIETRICH DA, 1993, 1093 ING DR DIETR

[2]

PFEIFERSCHALLER I, 1993, SURFACE ENG, P409

[3] DIFFERENTIAL LOAD FEED ANALYSIS - AN ENERGY-RELATED ALTERNATIVE TO THE INTERPRETATION OF HARDNESS INDENTATION MEASUREMENTS [J].

ROTHER, B ;

DIETRICH, DA .

PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1994, 142 (02) :389-407

[4] INTERFACE STRENGTH OF TITANIUM NITRIDE COATINGS ON HARDENED HIGH-SPEED STEEL [J].

ROTHER, B ;

LUNOW, T ;

LEONHARDT, G .

SURFACE & COATINGS TECHNOLOGY, 1995, 71 (03) :229-232

[5] EVALUATION OF COATING SUBSTRATE INTERFACE STRENGTH BY DIFFERENTIAL LOAD FEED ANALYSIS OF LOAD-INDENTATION MEASUREMENTS [J].

ROTHER, B ;

DIETRICH, DA .

THIN SOLID FILMS, 1994, 250 (1-2) :181-186

[6]

STOCK HR, 1993, CHARACTERISATION THI, P212

← 1 →