Structure and phase transformation of nano-scale particles of Fe-Ni alloys

被引:35
作者
Tadaki, T
Murai, Y
Koreeda, A
Nakata, Y
Hirotsu, Y
机构
[1] Inst. of Sci. and Indust. Research, Osaka University, Ibaraki, Osaka 567
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1996年 / 217卷
关键词
Fe-Ni alloys; phase transformation; nano-scale particles;
D O I
10.1016/S0921-5093(96)10295-1
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Atomic structure of nano-scale particles of Fe-rich Fe-Ni alloys and the phase transformation upon heating have been investigated by means of high resolution electron microscopy and electron diffraction. Fe-Ni nano-scale particles were prepared by vacuum-depositing master alloys with compositions of Fe-22.1, 25.2 and 28.6 at.% Ni on amorphous carbon ol alumina films at room temperature. As-deposited specimens were island-like, and composed of fine grains smaller than 5 nm in size, which were supposed to consist of the bce martensite and possibly of an oxide, NiFe2O4. Upon heating at 773 K, the reflections characteristic of these products disappeared, and a single set of reflect:ions appeared instead, which was identified to be of the fcc austenite. This phase transformation was observed even in specimens of the Fe-22.1 at.% Ni alloy, of which the austenite start temperature, A(s), is still roughly 50 K higher than the annealing temperature in the bulk state. Concurrently with this transformation, the initial fine grains coalesced to form isolated particles with average sizes of several nm in diameter. The austenitic particles thus formed were found to be entirely stable even when cooled to room temperature. This should also be noted, considering that the martensite start temperature, M(s), of the Fe-22.1 at.% Ni alloy is about 230 K higher than room temperature ill the bulk state. Then, it is considered that the austenite of the Fe-Ni alloys is stabilized by more than 200 K, when the size is reduced down to a nanometer scale. The origin of the remarkable stabilization of austenite remains unclear at present.
引用
收藏
页码:235 / 238
页数:4
相关论文
共 12 条
[1]  
CECH RE, 1956, T AM I MIN MET ENG, V206, P124
[2]  
CHEN YH, 1995, JPN J APPL PHYS 1, V34, P113, DOI 10.1143/JJAP.34.113
[3]   ATOM CLUSTERS - NEW APPLICATIONS OF HIGH-VOLTAGE ELECTRON-MICROSCOPY MICROLABORATORY TO MATERIALS SCIENCE [J].
FUJITA, H .
ULTRAMICROSCOPY, 1991, 39 (1-4) :369-381
[4]   MARTENSITIC TRANSFORMATIONS IN ULTRA-FINE PARTICLES OF METALS AND ALLOYS [J].
KAJIWARA, S ;
OHNO, S ;
HONMA, K .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1991, 63 (04) :625-644
[5]   AN ELECTRON DIFFRACTION STUDY ON CRYSTAL STRUCTURE OF A NEW MODIFICATION OF CHROMIUM [J].
KIMOTO, K ;
NISHIDA, I .
JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 1967, 22 (03) :744-&
[6]  
MCCLUNE WF, 1994, POWDER DIFFRACTION F, V44, P598
[7]   SPONTANEOUS ALLOYING OF COPPER INTO GOLD ATOM CLUSTERS [J].
MORI, H ;
KOMATSU, M ;
TAKEDA, K ;
FUJITA, H .
PHILOSOPHICAL MAGAZINE LETTERS, 1991, 63 (03) :173-178
[8]   LATTICE PARAMETERS OF MARTENSITE AND AUSTENITE IN FE-NI ALLOYS [J].
REED, RP ;
SCHRAMM, RE .
JOURNAL OF APPLIED PHYSICS, 1969, 40 (09) :3453-&
[10]   INTERFACE STRUCTURES OF GAMMA-IRON CRYSTALLITES EMBEDDED IN MAGNESIUM-OXIDE CRYSTALLINE FILMS [J].
TANAKA, N ;
YOSHIZAKI, F ;
KATZUDA, K ;
MIHAMA, K .
ACTA METALLURGICA ET MATERIALIA, 1992, 40 :S275-S280