Adsorption energetics of Ag on MgO(100)

被引：70

作者：

Larsen, JH ^{[1
]}

Ranney, JT ^{[1
]}

Starr, DE ^{[1
]}

Musgrove, JE ^{[1
]}

Campbell, CT ^{[1
]}

机构：

[1] Univ Washington, Dept Chem, Seattle, WA 98195 USA

来源：

PHYSICAL REVIEW B | 2001年 / 63卷 / 19期

关键词：

D O I：

10.1103/PhysRevB.63.195410

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper reports experimental measurements of the interaction of Ag with MgO(100) thin films grown on Mo(100). Both the adsorption energy and the sticking probability of Ag gas are reported as functions of silver coverage at room temperature. The initial heat of Ag adsorption is similar to 176 kJ/mol, but increases rapidly with coverage, reaching the bulk silver heat of sublimation of 285 kJ/mol by similar to8 ML. At the lowest coverages the sticking probability of silver is similar to0.94 and approaches 1.0 with increasing coverage. Auger electron spectroscopy indicates that silver grows as three-dimensional (3D) islands from submonolayer coverages. From the integral heat of adsorption, the adhesion energy of silver to MgO is estimated to be 0.3+/-0.3 J/m(2). The Ag-MgO(100) bond energy is estimated to be similar to 110 and similar to 15 kJ/mol within tiny 2D Ag clusters and large 3D Ag particles, respectively.

引用

页数：8

共 66 条

[21] Palladium nanocrystals on Al2O3:: Structure and adhesion energy [J].