Electrocatalytic oxidation of thiosulfate by metal hexacyanoferrate film modified electrodes

被引:90
作者
Chen, SM
机构
[1] Department of Chemical Engineering, Natl. Taipei Institute of Technology, Taipei 10643, No. 1, Sect. 3, Chung-Hsiao E. Road
来源
JOURNAL OF ELECTROANALYTICAL CHEMISTRY | 1996年 / 417卷 / 1-2期
关键词
thiosulfate; metal hexacyanoferrate film; modified electrodes; oxidation;
D O I
10.1016/S0022-0728(96)04720-1
中图分类号
O65 [分析化学];
学科分类号
070302 ; 081704 ;
摘要
The electrocatalytic oxidation of S2O32- by metal (iron(II), indium(III), nickel(II), and cobalt(II)) hexacyanoferrate film from consecutive cyclic voltammetry was investigated. The ferric hexacyanoferrate film catalyzed the rapid oxidation of thiosulfate after oxidizing the film [Fe(II)-CN-Fe(II)] to [Fe(III)-CN-Fe(III)]. The indium(III) hexacyanoferrate film has a similar catalytic mechanism. While nickel(II) hexacyanoferrate and cobalt(II) hexacyanoferrate films exhibit a different reaction mechanism, at the working electrode a more positive potential than E(Pa) of the metal(II) hexacyanoferrate(II)/metal(II) hexacyanoferrate(III) redox couple must be applied. The electrocatalytic oxidation of S4O62- to SO42- by ferric hexacyanoferrate film proceeds at a very slow reaction rate. The electrocatalytic oxidation of S2O32- was also performed using two layers of different metal hexacyanoferrate film modified electrodes. The results resemble the one layer metal hexacyanoferrate film modified electrode. A bicatalyst electrocatalytic reaction was performed using the rotating ring-disk electrode method. The electrocatalytic reduction current of S4O62- through Fe(I)(2-TMPyP) appears when S4O62- is produced from the electrocatalytic oxidation of S2O32- by metal hexacyanoferrate film.
引用
收藏
页码:145 / 153
页数:9
相关论文
共 38 条
[11]   POLYMERIZATION OF TRANSITION-METAL COMPLEXES IN SOLID POLYMER ELECTROLYTES [J].
HONDA, K ;
OCHIAI, J ;
HAYASHI, H .
JOURNAL OF THE CHEMICAL SOCIETY-CHEMICAL COMMUNICATIONS, 1986, (02) :168-170
[12]   PRUSSIAN BLUE CONTAINING NAFION COMPOSITE FILM AS RECHARGEABLE BATTERY [J].
HONDA, K ;
HAYASHI, H .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (06) :1330-1334
[13]   MECHANISMS OF CHARGE-TRANSFER AT THE CHEMICALLY DERIVATIZED INTERFACE - THE NI/[NIII(CN)FEII/III(CN)5]2-/1- SYSTEM AS AN ELECTROCATALYST [J].
HUMPHREY, BD ;
SINHA, S ;
BOCARSLY, AB .
JOURNAL OF PHYSICAL CHEMISTRY, 1987, 91 (03) :586-593
[14]   ELECTROCHEMISTRY OF POLYNUCLEAR TRANSITION-METAL CYANIDES - PRUSSIAN BLUE AND ITS ANALOGS [J].
ITAYA, K ;
UCHIDA, I ;
NEFF, VD .
ACCOUNTS OF CHEMICAL RESEARCH, 1986, 19 (06) :162-168
[15]   CATALYSIS OF THE REDUCTION OF MOLECULAR-OXYGEN TO WATER AT PRUSSIAN BLUE MODIFIED ELECTRODES [J].
ITAYA, K ;
SHOJI, N ;
UCHIDA, I .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1984, 106 (12) :3423-3429
[16]   COBALT(II) - CYANOMETALLATES AS NEW INORGANIC POLYMERIC MATERIALS FOR SURFACE-MODIFICATION OF SOME CONDUCTING SUBSTRATES [J].
JIANG, M ;
ZHOU, XY ;
ZHAO, ZF .
BERICHTE DER BUNSEN-GESELLSCHAFT-PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 1991, 95 (06) :720-727
[17]   CYCLIC VOLTAMMETRY STUDIES OF COPPER AND NICKEL HEXACYANOFERRATE IMMOBILIZED ON A SILICA-GEL SURFACE-COATED WITH TITANIUM(IV) OXIDE [J].
KUBOTA, LT ;
GUSHIKEM, Y .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1993, 362 (1-2) :219-225
[18]   APPLICATION OF CHELATE-FORMING RESIN AND MODIFIED GLASSY-CARBON ELECTRODE FOR SELECTIVE DETERMINATION OF IRON(III) BY LIQUID-CHROMATOGRAPHY WITH ELECTROCHEMICAL DETECTION [J].
KULESZA, PJ ;
BRAJTER, K ;
DABEKZLOTORZYNSKA, E .
ANALYTICAL CHEMISTRY, 1987, 59 (23) :2776-2780
[19]  
KUWANA T, 1983, J ELECTROCHM SOC, V130, P396
[20]   CATALYTIC ELECTROOXIDATION OF HYDRAZINE AT THE NICKEL FERRICYANIDE MODIFIED ELECTRODE - CAN AN ARRAY OF SURFACE BOUND ONE-ELECTRON REDOX CENTERS ACT IN CONCERT [J].
LIN, C ;
BOCARSLY, AB .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1991, 300 (1-2) :325-345