Heat treatment of thermal barrier coatings

被引:21
作者
Khan, AN
Lu, J
Liao, H
机构
[1] Univ Technol Troyes, LASMIS, F-10000 Troyes, France
[2] Univ Technol Belfort Montbeliard, LERMPS, Belfort, France
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2003年 / 359卷 / 1-2期
关键词
air plasma spraying (APS); thermal barrier coatings (TBC); heat treatment;
D O I
10.1016/S0921-5093(03)00372-1
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Thermal barrier coatings (TBCs) with CoNiCrAlY bond-coat and 0.3 mm thick zirconia top-coat were air plasma sprayed (APS) onto a nickel-base super alloy, Hastelloy-X and 316L stainless substrates. The samples were heat treated at different temperatures. The resulting microstructural features and fracture surfaces of the zirconia top-coat were studied by optical and electron microscopies. Formation of spinels was observed close to the thermal grown oxide (TGO)/top-coat interface, and it was noticed that this layer became thicker during long heat treatments. Top-coat phase stability was assessed by X-ray diffraction, and it was observed that for long heat treatments the top-coat transformed up to 26% into monoclinic phase. Residual stresses and relative interfacial toughness are also important factors, which affect the life of the TBC. They were determined by the hole drill method and by Vickers indentation. The relative interfacial toughness between the top-coat and bond-coat increased with increasing temperature for nickel-base super alloy substrates whereas, for stainless steel based TBCs it increased only up to 650 degreesC and then decreased with increasing temperature. For long heat treatments, the nickel-base TBCs showed that the interface between top-coat and bond-coat deteriorated with extended exposure time. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:129 / 136
页数:8
相关论文
共 29 条
[11]   THE FRACTURE ENERGY OF INTERFACES - AN ELASTIC INDENTATION TECHNIQUE [J].
DAVIS, JB ;
CAO, HC ;
BAO, G ;
EVANS, AG .
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (05) :1019-1024
[12]   QUASI-STATIC SOLID PARTICLE DAMAGE IN BRITTLE SOLIDS .1. OBSERVATIONS, ANALYSIS AND IMPLICATIONS [J].
EVANS, AG ;
WILSHAW, TR .
ACTA METALLURGICA, 1976, 24 (10) :939-956
[13]   YTTRIA-STABILIZED HAFNIA-ZIRCONIA THERMAL BARRIER COATINGS - THE INFLUENCE OF HAFNIA ADDITION ON TBC STRUCTURE AND HIGH-TEMPERATURE BEHAVIOR [J].
IBEGAZENE, H ;
ALPERINE, S ;
DIOT, C .
JOURNAL OF MATERIALS SCIENCE, 1995, 30 (04) :938-951
[14]   Measurement of the stress in oxide scales formed by oxidation of alumina-forming alloys [J].
Lipkin, DM ;
Clarke, DR .
OXIDATION OF METALS, 1996, 45 (3-4) :267-280
[15]   Mechanical properties of EB-PVD-thermal barrier coatings by nanoindentation [J].
Lugscheider, E ;
Bobzin, K ;
Bärwulf, S ;
Etzkorn, A .
SURFACE & COATINGS TECHNOLOGY, 2001, 138 (01) :9-13
[16]  
MENNIKE C, 1997, MATER SCI FORUM, V389, P251
[17]   Mechanisms controlling the performance and durability of thermal barrier coatings [J].
Mumm, DR ;
Evans, AG .
DURABLE SURFACES, 2001, 197 :199-230
[18]   THERMAL RESPONSE OF VARIOUS THERMAL BARRIER COATINGS IN A HIGH HEAT-FLUX ROCKET ENGINE [J].
NESBITT, JA .
SURFACE & COATINGS TECHNOLOGY, 1990, 43-4 (1-3) :458-469
[19]   Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings [J].
Rabiei, A ;
Evans, AG .
ACTA MATERIALIA, 2000, 48 (15) :3963-3976
[20]   Observation of subcritical spall propagation of a thermal barrier coating [J].
Sergo, V ;
Clarke, DR .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1998, 81 (12) :3237-3242