Magnetic-field-induced synthesis of magnetic γ-Fe2O3 nanotubes

被引：282

作者：

Wang, Junhong ^{[1
]}

Ma, Yanwei ^{[1
]}

Watanabe, Kazuo ^{[2
]}

机构：

[1] Chinese Acad Sci, Inst Elect Engn, Beijing 100080, Peoples R China

[2] Tohoku Univ, Inst Mat Res, High Field Lab Superconduct Mat, Sendai, Miyagi 9808577, Japan

来源：

CHEMISTRY OF MATERIALS | 2008年 / 20卷 / 01期

关键词：

D O I：

10.1021/cm702375e

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A method for synthesizing ferromagnetic γ-Fe2O3 nanotubes by a template process with the help of a magnetic field was presented. The direction of the magnetic field was perpendicular and parallel to the AAO membrane plane. A higher-magnification image revealed that the γFe2O3 nanotubes were arranged roughly parallel to one another. The center parts of the tube appeared bright in contrast to the wall, confirming their hollow structure of tubes. The hysteresis loops of nanotubes were performed using a SQUID magnetometer to investigate the magnetic properties of γ-Fe2O3 nanotubes. Phase identification, microstructure analysis, and magnetic measurements indicate that γ-Fe2O3 nanotubes have been formed under a 12T magnetic field. Magnetic properties of the nanotubes will be improved by the doping of Co to satisfy the application in high-density magnetic recordings.

引用

页码：20 / 22

页数：3

共 26 条

[11]

Kimura T, 2002, ADV MATER, V14, P1380, DOI 10.1002/1521-4095(20021002)14:19<1380::AID-ADMA1380>3.0.CO

[12]

2-V

[13] Application of high magnetic fields in advanced materials processing [J].

Ma Yanwei ;

Xiao Liye ;

Yan Luguang .

CHINESE SCIENCE BULLETIN, 2006, 51 (24) :2944-2950

[14] Effect of high magnetic field on the two-step martensitic-phase transition in Ni2MnGa [J].

Ma, YW ;

Awaji, S ;

Watanabe, K ;

Matsumoto, M ;

Kobayashi, N .

APPLIED PHYSICS LETTERS, 2000, 76 (01) :37-39

[15] EXISTENCE OF A DIRECT PHASE-TRANSFORMATION FROM HEMATITE TO MAGHEMITE [J].

MEILLON, S ;

DAMMAK, H ;

FLAVIN, E ;

PASCARD, H .

PHILOSOPHICAL MAGAZINE LETTERS, 1995, 72 (02) :105-110

[16] MAGNETIC SUSCEPTIBILITY OF ALPHA-FE203 AND ALPHA-FE203 WITH ADDED TITANIUM [J].

MORIN, FJ .

PHYSICAL REVIEW, 1950, 78 (06) :819-820

[17] Colloidal nanocrystal shape and size control: The case of cobalt [J].

Puntes, VF ;

Krishnan, KM ;

Alivisatos, AP .

SCIENCE, 2001, 291 (5511) :2115-2117

[18] Direct phase transformation from hematite to maghemite during high energy ball milling [J].

Randrianantoandro, N ;

Mercier, AM ;

Hervieu, M ;

Grenèche, JM .

MATERIALS LETTERS, 2001, 47 (03) :150-158

[19] Synthesis, morphology, and magnetic characterization of iron oxide nanowires and nanotubes [J].

Suber, L ;

Imperatori, P ;

Ausanio, G ;

Fabbri, F ;

Hofmeister, H .

JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (15) :7103-7109

[20]

Sudakar C, 2002, J MATER CHEM, V12, P107

← 1 2 3 →