Effect of microcrystallization on the cyclic oxidation behavior of β-NiAl intermetallics at 1000°C in air

被引：46

作者：

Yang, SL ^{[1
]}

Wang, FH ^{[1
]}

Wu, WT ^{[1
]}

机构：

[1] Acad Sinica, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China

来源：

INTERMETALLICS | 2001年 / 9卷 / 08期

关键词：

nickel aluminides; based on NiAl;

D O I：

10.1016/S0966-9795(01)00059-0

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The cyclic oxidation behavior of a magnetron sputtered NiAl microcrystalline coating was investigated at 1000 degreesC in air by TGA, and SEM in comparison with cast NiAl and NiAlY alloys. Results indicate that, for the cast NiAl alloy, mass loss is observed at about 40 cycles, implying the serious spallation occurred, while no spallation is detected for NiAlY alloy and NiAl coating for the whole test period. It is evident that. the scale adhesion is improved by the microcrystallization and the addition of Y. (C) 2001 Elsevier Science Ltd. All rights reserved.

引用

页码：741 / 744

页数：4

共 17 条

[1] OXIDATION BEHAVIOR OF NIAL .2. CAVITY FORMATION BENEATH THE OXIDE SCALE ON NIAL OF DIFFERENT STOICHIOMETRIES [J].

BRUMM, MW ;

GRABKE, HJ .

CORROSION SCIENCE, 1993, 34 (04) :547-&

[2]

BRUMM MW, 1992, CORROS SCI, V33, P1667

[3] SEGREGATION OF SULFUR DURING GROWTH OF OXIDE SCALES [J].

GRABKE, HJ ;

WIEMER, D ;

VIEFHAUS, H .

APPLIED SURFACE SCIENCE, 1991, 47 (03) :243-250

[4] OXIDE SCALE ADHESION AND IMPURITY SEGREGATION AT THE SCALE METAL INTERFACE [J].

HOU, PY ;

STRINGER, J .

OXIDATION OF METALS, 1992, 38 (5-6) :323-345

[5] On the formation of interfacial and internal voids in alpha-Al2O3 scales [J].

Pint, BA .

OXIDATION OF METALS, 1997, 48 (3-4) :303-328

[6] O-18/SIMS CHARACTERIZATION OF THE GROWTH-MECHANISM OF DOPED AND UNDOPED ALPHA-AL2O3 [J].

PINT, BA ;

MARTIN, JR ;

HOBBS, LW .

OXIDATION OF METALS, 1993, 39 (3-4) :167-195

[7] Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect [J].

Pint, BA .

OXIDATION OF METALS, 1996, 45 (1-2) :1-37

[8] The effect of various oxide dispersions on the phase composition and morphology of Al2O3 scales grown on beta-NiAl [J].

Pint, BA ;

Treska, M ;

Hobbs, LW .

OXIDATION OF METALS, 1997, 47 (1-2) :1-20

[9]

PROVENZANO V, 1988, SURF COAT TECH, V36, P36

[10] EFFECT OF THE THETA-ALPHA-AL2O3 TRANSFORMATION ON THE OXIDATION BEHAVIOR OF BETA-NIAL+ZR [J].

RYBICKI, GC ;

SMIALEK, JL .

OXIDATION OF METALS, 1989, 31 (3-4) :275-304

← 1 2 →