Touching the properties of NbTi by carbon doped tapes with mechanically alloyed MgB2

被引：120

作者：

Herrmann, Marko ^{[1
]}

Haessler, Wolfgang ^{[1
]}

Rodig, Christian ^{[1
]}

Gruner, Wolfgang ^{[1
]}

Holzapfel, Bernhard ^{[1
]}

Schultz, Ludwig ^{[1
]}

机构：

[1] IFW Dresden, Inst Met Mat, D-01171 Dresden, Germany

来源：

APPLIED PHYSICS LETTERS | 2007年 / 91卷 / 08期

关键词：

D O I：

10.1063/1.2773942

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Combining mechanical alloying and powder-in-tube processing is a promising way to obtain tapes with excellent properties. Taking advantage of the properties of nanocrystalline precursor powders, it was possible to obtain J(c) values of 10(4) A/cm(2) at 12.1 T and 4.2 K. Evidential substitution of carbon into the MgB2 changed the electron scattering and therefore raised the B-c2 up to 12 T at 10 K. Systematic investigation on the influence of the heat treatment showed that, although an interfering Fe2B reaction layer was formed, an excellent J(c) of 10(4) A/cm(2) at 14.3 T and 4.2 K was achieved.

引用

页数：3

共 17 条

[11] Superconductivity at 39 K in magnesium diboride [J].

Nagamatsu, J ;

Nakagawa, N ;

Muranaka, T ;

Zenitani, Y ;

Akimitsu, J .

NATURE, 2001, 410 (6824) :63-64

[12]

SCHUBERT M, 2006, SUPERCOND SCI TECH, V19, P512

[13] Improved upper critical field in bulk-form magnesium diboride by mechanical alloying with carbon [J].

Senkowicz, BJ ;

Giencke, JE ;

Patnaik, S ;

Eom, CB ;

Hellstrom, EE ;

Larbalestier, DC .

APPLIED PHYSICS LETTERS, 2005, 86 (20) :1-3

[14]

VANWEEREN H, 2007, THESIS U TWENTE

[15]

VILLARS P, 1991, PEARSONS HDB CRYSTAL, V2, P1555

[16] Enhancement of Hc2 and Jc by carbon-based chemical doping [J].

Yeoh, W. K. ;

Dou, S. X. .

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2007, 456 (1-2) :170-179

[17] Strong pinning and high critical current density in carbon nanotube doped MgB2 [J].

Yeoh, WK ;

Horvat, J ;

Dou, SX ;

Keast, V .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (09) :S572-S577

← 1 2 →