Manganese ferrite synthesized from Mn(II) acetate plus hematite freeze-dried powders

被引：19

作者：

Bellini, J. V. ^{[1
]}

de Medeiros, S. N. ^{[1
]}

Ponzoni, A. L. L. ^{[1
]}

Longen, F. R. ^{[1
]}

de Melo, M. A. C. ^{[1
]}

Paesano, A., Jr. ^{[1
]}

机构：

[1] Univ Estadual Maringa, Dept Fis, BR-87020900 Maringa, Parana, Brazil

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2007年 / 105卷 / 01期

关键词：

freeze-drying; manganese ferrite; thermal analysis; Mossbauer spectroscopy;

D O I：

10.1016/j.matchemphys.2007.04.005

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Freeze-drying was used to obtain a homogeneous fine powder containing (CH3COO)(2)Mn-2H2O and ct-Fe2O3 (molar ratio Fe:Mn = 3: 1), which was thermally treated for 2 h in N-2 atmosphere, at 400 degrees C. This composite system was further annealed for 4 h in the same atmosphere, either at 700 degrees C or at 1000 degrees C. The 700 degrees C annealed sample was thermally treated in air at 1200 degrees C and then rapidly quenched. The phase transformations that occurred in the freeze-dried and heat-treated powders were investigated by thermal analyses, X-ray diffractometry, scanning electron microscopy and Mossbauer spectroscopy. Results showed that MnO-alpha-Fe2O3-Fe3O4 compounds were obtained after the first heat-treatment. Samples subsequently annealed in N atmosphere revealed the formation of Fe-rich manganese ferrites and manganowUstite phases. However, a single spinel phase was obtained for the sample that had been annealed and quenched in air. (c) 2007 Elsevier B.V. All rights reserved.

引用

页码：92 / 98

页数：7

共 28 条

[21] KINETIC AND MECHANISTIC STUDY OF THE NONISOTHERMAL DECOMPOSITION OF MANGANESE(II) ACETATE TETRAHYDRATE [J].

MOHAMED, MA ;

HALAWY, SA .

THERMOCHIMICA ACTA, 1994, 242 :173-186

[22] Structural-chemical transformations of α-Fe2O3 upon transport reduction [J].

Murin, IV ;

Smirnov, VM ;

Voronkov, GP ;

Semenov, VG ;

Povarov, VG ;

Sinel'nikov, BM .

SOLID STATE IONICS, 2000, 133 (3-4) :203-210

[23]

Newkirk A. E., 1971, Thermochimica Acta, V2, P1, DOI 10.1016/0040-6031(71)85021-9

[24] THERMAL AND CHEMICAL EVENTS IN THE DECOMPOSITION COURSE OF MANGANESE COMPOUNDS [J].

NOHMAN, AKH ;

ISMAIL, HM ;

HUSSEIN, GAM .

JOURNAL OF ANALYTICAL AND APPLIED PYROLYSIS, 1995, 34 (02) :265-278

[25] Mechano synthesis and process characterization of nanostructured manganese ferrite [J].

Padella, F ;

Alvani, C ;

La Barbera, A ;

Ennas, G ;

Liberatore, R ;

Varsano, F .

MATERIALS CHEMISTRY AND PHYSICS, 2005, 90 (01) :172-177

[26] Effect of foreign cation of Zn(II) or Mn(II) ion in FeO-wustite on its disproportionation reaction below 575°C [J].

Sano, T ;

Tsuji, M ;

Tamaura, Y .

SOLID STATE IONICS, 1997, 104 (3-4) :311-317

[27] PREPARATION OF MANGANESE FERRITE FINE PARTICLES FROM AQUEOUS-SOLUTION [J].

TANG, ZX ;

SORENSEN, CM ;

KLABUNDE, KJ ;

HADJIPANAYIS, GC .

JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1991, 146 (01) :38-52

[28] Neural network approximation of iron oxide reduction process [J].

Wiltowski, T ;

Piotrowski, K ;

Lorethova, H ;

Stonawski, L ;

Mondal, K ;

Lalvani, SB .

CHEMICAL ENGINEERING AND PROCESSING-PROCESS INTENSIFICATION, 2005, 44 (07) :775-783

← 1 2 3 →