Enhanced model of partial crack closure for correlation of R-ratio effects in aluminum alloys

被引：128

作者：

Kujawski, D ^{[1
]}

机构：

[1] Western Michigan Univ, Coll Engn & Appl Sci, Dept Mech & Aeronaut Engn, Kalamazoo, MI 49008 USA

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2001年 / 23卷 / 02期

关键词：

crack growth; R-ratio effects; crack closure; effective stress intensity;

D O I：

10.1016/S0142-1123(00)00085-2

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper, an enhancement of Donald and Paris partial crack closure model is proposed. The enhancement is based on the argument that an apparent effectiveness of the crack closure phenomenon is dependent upon K-max and the crack tip opening profile. A transition function is used in order to evolve from Donald and Paris' partial crack closure model at the near-threshold region to the conventional Elber's closure approach at the Paris region. The model correlates fairly well the R-ratio effects on fatigue crack growth rate at low and intermediate stress intensities for aluminum alloys. (C) 2001 Elsevier Science Ltd. All rights reserved.

引用

页码：95 / 102

页数：8

共 18 条

[1]

[Anonymous], STRESS ANAL CRACKS H

[2]

Donald K, 1999, INT J FATIGUE, V21, pS47

[3]

Elber W., 1971, AMAGE TOLERANCE AIRC, P230, DOI DOI 10.1520/STP486-EB

[4] SURFACE DAMAGE AND NEAR-THRESHOLD FATIGUE CRACK-GROWTH IN A NI-BASE SUPER-ALLOY IN VACUUM [J].

KING, JE .

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1982, 5 (02) :177-188

[5] SLOW FATIGUE CRACK GROWTH AND THRESHOLD BEHAVIOR IN AIR AND VACUUM OF COMMERCIAL ALUMINUM-ALLOYS [J].

KIRBY, BR ;

BEEVERS, CJ .

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1979, 1 (02) :203-&

[6] EFFECT OF STRESS CYCLE ASYMMETRY ON FATIGUE CRACK GROWTH [J].

KLESNIL, M ;

LUKAS, P .

MATERIALS SCIENCE AND ENGINEERING, 1972, 9 (04) :231-&

[7] A FATIGUE CRACK-GROWTH MODEL WITH LOAD RATIO EFFECTS [J].

KUJAWSKI, D ;

ELLYIN, F .

ENGINEERING FRACTURE MECHANICS, 1987, 28 (04) :367-378

[8]

LANG M, 1998, FATIGUE FRACTURE MEC, V29

[9]

Lawson L, 1999, INT J FATIGUE, V21, pS15

[10]

MACHA DE, 1979, P SOC EXPT STRESS AN, V36, P207

← 1 2 →