Phase separation in a two-dimensional Co-Cr alloy

被引:11
作者
Kahng, SJ
Choi, YJ
Park, JY
Kuk, Y [1 ]
机构
[1] ISRC, Ctr Sci Nanometer Scale, Natl Creat Res Initiat, Seoul 151742, South Korea
[2] Seoul Natl Univ, Dept Phys, Seoul 151742, South Korea
关键词
D O I
10.1063/1.123490
中图分类号
O59 [应用物理学];
学科分类号
摘要
Two-dimensional phase separation in a Co-Cr random binary alloy on a W(110) surface was confirmed with ultra-high-vacuum scanning tunneling microscopy. With 1.1 ML Co and 0.1 ML Cr co-deposited at room temperature, the film shows a kinetically limited structure. Upon annealing, phase separation between Co and Cr-rich phases of similar to 100 Angstrom size was observed. Evidence of compositional inhomogeneity was observed in Cr-rich phases but not in Co-rich phases. (C) 1999 American Institute of Physics. [S0003-6951(99)04008-5].
引用
收藏
页码:1087 / 1089
页数:3
相关论文
共 18 条
[1]  
BERLOWITZ PJ, 1989, SURF SCI, V209, P345, DOI 10.1016/0039-6028(89)90080-0
[2]   CO-CR FILMS WITH PERPENDICULAR MAGNETIC-ANISOTROPY [J].
COUGHLIN, TM ;
JUDY, JH ;
WUORI, ER .
IEEE TRANSACTIONS ON MAGNETICS, 1981, 17 (06) :3169-3171
[3]   EPITAXIAL STRAIN AND MAGNETIC-ANISOTROPY IN ULTRATHIN CO FILMS ON W(110) [J].
FRITZSCHE, H ;
KOHLHEPP, J ;
GRADMANN, U .
PHYSICAL REVIEW B, 1995, 51 (22) :15933-15941
[4]   PHOTOEMISSION AND ELECTRONIC-STRUCTURE OF COBALT [J].
HEIMANN, P ;
MARSCHALL, E ;
NEDDERMEYER, H ;
PESSA, M ;
ROLOFF, HF .
PHYSICAL REVIEW B, 1977, 16 (06) :2575-2583
[5]   High recording performance of Co-Cr medium sputter-deposited at high Ar pressure and high substrate temperature [J].
Honda, N ;
Yanase, S ;
Ouchi, K ;
Iwasaki, SI .
JOURNAL OF APPLIED PHYSICS, 1996, 79 (08) :5362-5364
[6]   3-DIMENSIONAL ATOM-PROBE ANALYSIS OF A SPUTTER-DEPOSITED CO-CR THIN-FILM [J].
HONO, K ;
YEH, K ;
MAEDA, Y ;
SAKURAI, T .
APPLIED PHYSICS LETTERS, 1995, 66 (13) :1686-1688
[7]   FABRICATION OF LOW-NOISE MEDIA-A MANUFACTURING PERSPECTIVE [J].
JOHNSON, KE ;
MAHLKE, JB ;
SCHULZ, KJ ;
WALL, AC .
IEEE TRANSACTIONS ON MAGNETICS, 1993, 29 (01) :215-222
[8]   SCANNING TUNNELING MICROSCOPE INSTRUMENTATION [J].
KUK, Y ;
SILVERMAN, PJ .
REVIEW OF SCIENTIFIC INSTRUMENTS, 1989, 60 (02) :165-180
[9]   SEGREGATED MICROSTRUCTURE IN SPUTTERED CO-CR FILM REVEALED BY SELECTIVE WET ETCHING [J].
MAEDA, Y ;
ASAHI, M .
JOURNAL OF APPLIED PHYSICS, 1987, 61 (05) :1972-1978
[10]   INITIAL GROWTH OF AU ON NI(110) - SURFACE ALLOYING OF IMMISCIBLE METALS [J].
NIELSEN, LP ;
BESENBACHER, F ;
STENSGAARD, I ;
LAEGSGAARD, E ;
ENGDAHL, C ;
STOLTZE, P ;
JACOBSEN, KW ;
NORSKOV, JK .
PHYSICAL REVIEW LETTERS, 1993, 71 (05) :754-757