Morphology and melting of truncated single crystals of linear polyethylene

被引:45
作者
Hocquet, S
Dosière, M
Thierry, A
Lotz, B
Koch, MHJ
Dubreuil, N
Ivanov, DA
机构
[1] Univ Mons, Lab Physicochim Polymeres, B-7000 Mons, Belgium
[2] Inst Charles Sadron, F-67083 Strasbourg, France
[3] DESY, EMBL, European Mol Biol Lab, Hamburg Outstn, D-22603 Hamburg, Germany
[4] Free Univ Brussels, Polymer Phys Lab, B-1050 Brussels, Belgium
关键词
D O I
10.1021/ma034315l
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The thickness of (110) and (200) sectors in truncated single crystals of linear polyethylene grown from dilute n-octane solution at 95 degreesC was measured by atomic force microscopy (AFM) in tapping mode. The (110) sector was found to be 1.1 nm thicker than the (200) sector. This can be explained b a somewhat smaller tilt angle of the chains with respect to the basal plane of the crystal. The tilt of the chains in (110) and (200) sectors, obtained by electron diffraction, is 22degrees and 30degrees, respectively. This implies that the length of the stem, i.e., the length of the straight part of the chains between two consecutive folds, is identical in both sectors of the truncated single crystals. The melting of individual LPE truncated single crystals was revisited by AFM. The melting temperatures of the (200) and (110) sectors are 124.9 and 125.9 +/- 0.3 degreesC, respectively. The lamellar thickness distribution calculated from AFM pictures clearly indicates that reorganization into thicker lamellae takes place during heating. The melting of mats of filtration of truncated LPE single crystals has also been investigated by time-resolved small-angle X-ray scattering (SAXS) and differential scanning calorimetry (DSC). The melting curve of LPE single crystals generally exhibits two endotherms. The low and the high melting temperature endotherms are characteristic of single crystals formed from dilute solution and reorganized thicker lamellae during the heating ramp, respectively. Time-resolved SAXS measurements data indicate that two populations of lamellar crystals coexist between 122 and 128 degreesC. The maximum value observed for the lamellar thickness of the recrystallized material is 30 nm, i.e., twice the initial lamellar thickness of single crystals obtained from dilute solution. There is good agreement between the thicknesses of the crystalline layers obtained from the SAXS data and the values calculated from the Gibbs-Thomson relationship using experimental values of the peak temperature of the two endotherms.
引用
收藏
页码:8376 / 8384
页数:9
相关论文
共 43 条
[21]   X-RAY-DIFFRACTION AND SCATTERING ON DISORDERED-SYSTEMS USING SYNCHROTRON RADIATION [J].
KOCH, MHJ ;
BORDAS, J .
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH, 1983, 208 (1-3) :461-469
[22]   Overlapping of different rearrangement mechanisms upon annealing for solution-crystallized polyethylene [J].
Matsuda, H ;
Aoike, T ;
Uehara, H ;
Yamanobe, T ;
Komoto, T .
POLYMER, 2001, 42 (11) :5013-5021
[23]  
MAZUR J, 1982, B AM PHYS SOC, V27, P289
[24]   MOLECULAR MECHANICS OF POINT DEFECTS IN POLYETHYLENE [J].
MCMAHON, PE ;
MCCULLOUGH, RL ;
SCHLEGEL, AA .
JOURNAL OF APPLIED PHYSICS, 1967, 38 (11) :4123-+
[25]   RAMAN FREQUENCIES OF NORMAL-PARAFFIN MOLECULES [J].
MIZUSHIMA, SI ;
SIMANOUTI, T .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1949, 71 (04) :1320-1324
[26]   ATOMIC-FORCE MICROSCOPY OF SOLUTION-GROWN POLYETHYLENE SINGLE-CRYSTALS [J].
NAKAGAWA, Y ;
HAYASHI, H ;
TAKAHAGI, T ;
SOEDA, F ;
ISHITANI, A ;
TODA, A ;
MIYAJI, H .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1994, 33 (6B) :3771-3774
[27]   HOLLOW PYRAMIDAL CRYSTALS OF POLYETHYLENE AND A MECHANISM OF GROWTH [J].
NIEGISCH, WD ;
SWAN, PR .
JOURNAL OF APPLIED PHYSICS, 1960, 31 (11) :1906-1910
[28]   SOLUTION CRYSTALLIZATION OF POLYETHYLENE AT HIGH-TEMPERATURES .1. LATERAL CRYSTAL HABITS [J].
ORGAN, SJ ;
KELLER, A .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (05) :1571-1585
[29]   CHAIN CONFORMATIONS ON SURFACE OF POLYETHYLENE SINGLE-CRYSTALS [J].
OYAMA, TO ;
SHIOKAWA, K ;
ISHIMARU, T .
JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1973, B008 (1-2) :229-239
[30]   CRYSTAL-GROWTH KINETICS AND THE LATERAL HABITS OF POLYETHYLENE CRYSTALS [J].
PASSAGLIA, E ;
KHOURY, F .
POLYMER, 1984, 25 (05) :631-644