Preparation and characterization of calcium phosphate biomaterials

Calcium phosphate cement (CPC) samples have been prepared with a mixture of monocalciumphosphate monohydrate (MCPM) and calcium carbonate (CC) powders, in stechiometric moles ratio 1:2.5 to obtain a Ca/P ratio of about 1.67 typical of hydroxyapatite (HAp), with or without addition of HAp. All specimens are incubated at 30 degrees C in a steam saturated air environment for 3, 6 and 15 days respectively, afterwards dried and stored under nitrogen. The calcium phosphate samples have been characterized by X-ray diffraction (XRD), Vickers hardness test (HV), diametral compression (d.c.), strength compression, and porosity evaluation. MCPM/CC mixture has a 30% HAp final concentration and is characterized by higher porosity (amount 78%) and mechanical properties useful as filler in bone segments without high mechanical stress.