Review of a chemical approach to YBa2Cu3O7-x-coated, superconductors -: metalorganic deposition using trifluoroacetates

Large-area, uniform, high critical current density (J(c)) YBa2Cu3O7-x (YBCO) superconductor films are now routinely obtained by metalorganic deposition using trifluoroacetates (TFA-MOD). This method does not require any expensive vacuum apparatus at any time during the whole process. Thus, TFA-MOD is regarded as one of the most suitable candidates for fabricating a YBCO tape for many high-power applications. This method originated from an electron beam process using BaF2 developed by Mankiewich et al. Afterwards, Gupta et al reported using TFA-MOD to prepare a similar precursor film. These two ex situ processes used fluorides instead of BaCO3 to avoid the fatal deterioration in J(c), which is caused in the resulting films through metal carboxylic groups. Fluorides not only avoid such deterioration but also lead to perfectly c-axis-oriented epitaxial crystal growth. In conventional metalorganic deposition, nucleation in the precursor film causes random orientation in the resulting film. However, in TFA-MOD, nanocrystallites in the precursor film never cause such disorder. Furthermore, during the firing process of TFA-MOD, water and HF gas diffuse quickly between the film surface and growth front of the YBCO layer. This diffusion never limits the growth rate of YBCO. What distinguishes TFA-MOD from conventional metalorganic deposition? What happens during heat treatment? In this paper, we discuss all the TFA-MOD processes and the peculiar growth scheme of the YBCO layer in TFA-MOD using the model of a quasi-liquid network. In addition, we review the history of TFA-MOD and recent results and discuss the prospects of future applications.