Preparation of negative electrodes for lithium-ion rechargeable battery by pressure-pulsed chemical vapor infiltration of pyrolytic carbon into electro-conductive forms

被引:24
作者
Ohzawa, Y [1 ]
Mitani, M [1 ]
Suzuki, T [1 ]
Gupta, V [1 ]
Nakajima, T [1 ]
机构
[1] Aichi Inst Technol, Dept Appl Chem, Toyota 4700392, Japan
关键词
chemical vapor deposition; chemical vapor infiltration; pyrolytic carbon; lithium-ion battery;
D O I
10.1016/S0378-7753(03)00394-X
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The plate-type negative electrodes for lithium-ion rechargeable battery were prepared by pressure-pulsed chemical vapor infiltration of pyrolytic carbon (pyrocarbon) into two sorts of conductive porous forms, that is, the carbonized paper (A) and the TiN-coated paper (B), as the conductive fillers and/or current collectors. The electrodes had the three-dimensionally continuous current paths in the pyrocarbon-based anodes without the organic binders and the additional conductive filters. The pyrocarbon in sample (A) had the relatively high crystallinity, whereas the pyrocarbon in sample (B) was disordered. Sample (B) possessed higher surface area and larger pore volume with mesopores per mass of of 1.5-10 nm. especially below 3 nm, than that of sample (A). The capacity of pyrocarbon in sample (B) was 460 mA h g(-1) pyrocarbon at a current density of 25 mA g(-1), reflecting the disordered microstructure of pyrocarbon film. And 80% of the capacity was maintained even at 1000 mA g(-1). The capacity of pyrocarbon in sample (A) was estimated at similar to300 mA h g(-1), which was lower than that of sample (B). However, sample (A) showed higher Coulombic efficiency at first cycle (i.e. 85%) than that of sample (B), which would result from the high crystallinity, laminar microstructure and low surface area of pyrocarbon in sample (A). (C) 2003 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:153 / 161
页数:9
相关论文
共 27 条
  • [1] Ahn S, 1998, ELECTROCHEM SOLID ST, V1, P111
  • [2] [Anonymous], P 3 INT C CVD NEW YO
  • [3] FABRICATION OF CERAMIC COMPOSITES - FORCED CVI
    BESMANN, TM
    MCLAUGHLIN, JC
    LIN, HT
    [J]. JOURNAL OF NUCLEAR MATERIALS, 1995, 219 : 31 - 35
  • [4] BESMANN TM, 1990, P 11 INT C CVD EL SO, P482
  • [5] Cheristin F., 1979, P 5 INT C CVD EL SOC, P499
  • [6] INTERFACE CHARACTERIZATION BY TEM, AES AND SIMS IN TOUGH SIC (EX-PCS) FIBER-SIC (CVI) MATRIX COMPOSITES WITH A BN INTERPHASE
    DUGNE, O
    PROUHET, S
    GUETTE, A
    NASLAIN, R
    FOURMEAUX, R
    KHIN, Y
    SEVELY, J
    ROCHER, JP
    COTTERET, J
    [J]. JOURNAL OF MATERIALS SCIENCE, 1993, 28 (13) : 3409 - 3422
  • [7] Golecki I, 1996, ELEC SOC S, V96, P547
  • [8] Effects of synthesis temperature on the electrochemical characteristics of pyrolytic carbon for anodes of lithium-ion secondary batteries
    Han, YS
    Yu, JS
    Park, GS
    Lee, JY
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1999, 146 (11) : 3999 - 4004
  • [9] BEHAVIOR OF BC2N TREATED UNDER VARIOUS TEMPERATURES AS A NEGATIVE ELECTRODE MATRIX FOR RECHARGEABLE LITHIUM BATTERIES
    ISHIKAWA, M
    MORITA, M
    HANADA, T
    MATSUDA, Y
    KAWAGUCHI, M
    [J]. DENKI KAGAKU, 1993, 61 (12): : 1395 - 1402
  • [10] Densification of carbon/carbon composites by pulse chemical vapor infiltration
    Jeong, HJ
    Park, HD
    Lee, JD
    Park, JO
    [J]. CARBON, 1996, 34 (03) : 417 - 421