Micropatterning of ZnO nanoarrays by forced hydrolysis of anhydrous zinc acetate

被引：45

作者：

Hu, Xiulan ^{[1
]}

Masuda, Yoshitake ^{[1
]}

Ohji, Tatsuki ^{[1
]}

Kato, Kazumi ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Moriyama Ku, Nagoya, Aichi 4638560, Japan

来源：

LANGMUIR | 2008年 / 24卷 / 14期

关键词：

D O I：

10.1021/la8006348

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Micropatterns of ZnO nanoarrays were simply and successfully fabricated in an aqueous solution without any high-temperature treatment and/or expensive catalyst. In situ forced hydrolysis of patterned anhydrous zinc acetate, derived by ultraviolet irradiation with a photomask, resulted in heterogeneous nucleation and growth to form ZnO nanoarrays. Micropatterns of ZnO nanoarrays were characterized by FE-SEM and XRD. ZnO nanoarrays were well site-selectively deposited on anhydrous zinc acetate coated regions at 88 degrees C. HR-TEM clarified the formation mechanism in which anhydrous zinc acetate showed a tendency of forced hydrolyzation to ZnO nanocrystals at the initial stage in the reaction solution.

引用

页码：7614 / 7617

页数：4

共 37 条

[1]

CAPILLA AV, 1979, CRYST STRUCT COMMUN, V8, P795

[2] Growth of single crystal ZnO nanowires using sputter deposition [J].

Chiou, WT ;

Wu, WY ;

Ting, JM .

[3] Morphology evolution of ZnO thin films from aqueous solutions and their application to solar cells [J].

Gao, YF ;

Nagai, M .

LANGMUIR, 2006, 22 (08) :3936-3940

[4] General route to vertical ZnO nanowire arrays using textured ZnO seeds [J].

Greene, LE ;

Law, M ;

Tan, DH ;

Montano, M ;

Goldberger, J ;

Somorjai, G ;

Yang, PD .

NANO LETTERS, 2005, 5 (07) :1231-1236

[5] Low-temperature wafer-scale production of ZnO nanowire arrays [J].

Greene, LE ;

Law, M ;

Goldberger, J ;

Kim, F ;

Johnson, JC ;

Zhang, YF ;

Saykally, RJ ;

Yang, PD .

ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2003, 42 (26) :3031-3034

[6] Solution-grown zinc oxide nanowires [J].

Greene, Lori E. ;

Yuhas, Benjamin D. ;

Law, Matt ;

Zitoun, David ;

Yang, Peidong .

INORGANIC CHEMISTRY, 2006, 45 (19) :7535-7543

[7] Hydrothermal growth of well-aligned ZnO nanorod arrays: Dependence of morphology and alignment ordering upon preparing conditions [J].

Guo, M ;

Diao, P ;

Cai, SM .

JOURNAL OF SOLID STATE CHEMISTRY, 2005, 178 (06) :1864-1873

[8] MICROEMULSION MEDIATED SYNTHESIS OF ZINC-OXIDE NANOPARTICLES FOR VARISTOR STUDIES [J].

HINGORANI, S ;

PILLAI, V ;

KUMAR, P ;

MULTANI, MS ;

SHAH, DO .

MATERIALS RESEARCH BULLETIN, 1993, 28 (12) :1303-1310

[9] Room-temperature ultraviolet light-emitting zinc oxide micropatterns prepared by low-temperature electrodeposition and photoresist [J].

Izaki, M ;

Watase, S ;

Takahashi, H .

APPLIED PHYSICS LETTERS, 2003, 83 (24) :4930-4932

[10]

Kind H, 2002, ADV MATER, V14, P158, DOI 10.1002/1521-4095(20020116)14:2<158::AID-ADMA158>3.0.CO

← 1 2 3 4 →