A comparative study of two inward grown Pt modified Al diffusion coatings on a single crystal Ni base superalloy

被引：80

作者：

Angenete, J ^{[1
]}

Stiller, K

机构：

[1] Chalmers Univ Technol, Dept Expt Phys, SE-41296 Gothenburg, Sweden

[2] Univ Gothenburg, SE-41296 Gothenburg, Sweden

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2001年 / 316卷 / 1-2期

关键词：

platinum modified aluminide diffusion coatings; RT22; SS82A; CMSX-4; high temperature oxidation;

D O I：

10.1016/S0921-5093(01)01236-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Two inward grown Pt modified aluminide diffusion coatings (RT22 and SS82A) on the same Ni-based superalloy substrate (CMSX-4) have been studied. The specimens were oxidised in still laboratory air at 1050 degreesC for times up to 2000 h and investigated by gravimetry. Specimens oxidised up to 500 h were studied by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive X-ray spectrometry (EDS). The gravimetric investigations revealed that the oxide on RT22 grew faster than the oxide on SS82A. Moreover, it was found that in the as-coated condition, both coatings contained precipitates of alpha -W, alpha -Cr, mu -phase and sigma -phase. After short time heat treatment at 1050 degreesC, only mu -phase precipitates were present. The volume fraction of the precipitates was measured and compared for different heat treatments. Compositional profiles across the coatings were acquired by TEM-EDS before and after heat treatment. They showed that considerable redistribution of elements takes place during oxidation and the initially steep Pt and Al profiles became smeared out. The RT22 coating formed gamma ' -Ni3Al grains at the coating/oxide interface. (C) 2001 Elsevier Science B.V. All rights reserved.

引用

页码：182 / 194

页数：13

共 34 条

[11] MECHANISMS OF FORMATION OF DIFFUSION ALUMINIDE COATINGS ON NICKEL-BASE SUPERALLOYS [J].

GOWARD, GW ;

BOONE, DH .

OXIDATION OF METALS, 1971, 3 (05) :475-&

[12]

GOWARD GW, 1988, T ASME, V110, P150

[13]

HATTESTRAND M, 2001, IN PRESS MICRON

[14] ALUMINIZATION OF PLATINUM AND PLATINUM-COATED IN-738 [J].

JACKSON, MR ;

RAIRDEN, JR .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (11) :1697-1707

[15]

JACKSON MR, 1978, METALLURGY CERAMICS, V1, P423

[16] PARTITION OF ALLOYING ELEMENTS BETWEEN GAMMA-(A1), GAMMA(')-(L12), AND BETA-(B2) PHASES IN NI-AL BASE SYSTEMS [J].

JIA, CC ;

ISHIDA, K ;

NISHIZAWA, T .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (03) :473-485

[17]

Joseph A.D., 1963, U. S. Patent, Patent No. [3, 102, 044, 3102044]

[18]

KORINKO PS, 1996, P INT GAS TURB AER C, P1

[19]

LEHNERT G, 1972, ELECTRODEP SURF TREA, V189, P71

[20] HIGH-TEMPERATURE CORROSION OF ALUMINA-FORMING COATINGS FOR SUPERALLOYS [J].

MEIER, GH ;

PETTIT, FS .

SURFACE & COATINGS TECHNOLOGY, 1989, 39 (1-3) :1-17

← 1 2 3 4 →