Thermally activated mechanisms of hydrogen abstraction by growth precursors during plasma deposition of silicon thin films

Hydrogen abstraction by growth precursors is the dominant process responsible for reducing the hydrogen content of amorphous silicon thin films grown from SiH4 discharges at low temperatures. Besides direct (Eley-Rideal) abstraction, gas-phase radicals may first adsorb on the growth surface and abstract hydrogen in a subsequent process, giving rise to thermally activated precursor-mediated (PM) and Langmuir-Hinshelwood (LH) abstraction mechanisms. Using results of first-principles density functional theory (DFT) calculations on the interaction of SiH3 radicals with the hydrogen-terminated Si(001)-(2 x 1) surface, we show that precursor-mediated abstraction mechanisms can be described by a chemisorbed SiH3 radical hopping between overcoordinated surface Si atoms while being weakly bonded to the surface before encountering a favorable site for hydrogen abstraction. The calculated energy barrier of 0.39 eV for the PM abstraction reaction is commensurate with the calculated barrier of 0.43-0.47 eV for diffusion of SiH3 on the hydrogen-terminated Si(001)-(2 x 1) surface, which allows the radical to sample the entire surface for hydrogen atoms to abstract. In addition, using the same type of DFT analysis we have found that LH reaction pathways involve bond breaking between the silicon atoms of the chemisorbed SiH3 radical and the film prior to hydrogen abstraction. The LH reaction pathways exhibit energy barriers of 0.76 eV or higher, confining the abstraction only to nearest-neighbor hydrogens. Furthermore, we have found that LH processes compete with radical desorption from the hydrogen-terminated Si(001)-(2 x 1) surface and may be suppressed by the dissociation of chemisorbed SiH3 radicals into lower surface hydrides. Analysis of molecular-dynamics simulations of the growth process of plasma deposited silicon films have revealed that qualitatively similar pathways for thermally activated hydrogen abstraction also occur commonly on the amorphous silicon growth surface. (C) 2005 American Institute of Physics.