Cu-Hf-Ti-Ag-Ta bulk metallic glass composites and their properties

被引:91
作者
Bian, Z [1 ]
Kato, H
Qin, CL
Zhang, W
Inoue, A
机构
[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
[2] Japan Sci & Technol Agcy, Sendai, Miyagi 9808577, Japan
关键词
bulk metallic glass composite; composition; dendrite; mechanical property; indentation;
D O I
10.1016/j.actamat.2005.01.015
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Multi-component (Cu-0.50)Hf0.35Ti0.10 Ag-0.05)(100-x) Ta-x(x = 0, 1, 3, 5, 8, 12) bulk metallic glass (BMG) composites containing in situ formed dendrites were prepared successfully. With increasing Ta content, both compressive fracture strength (sigma(f)) and elasticplastic strain (epsilon(f)) increase from 2180 MPa and 2.1% for x = 0, to 2770 MPa and 19.2% for x = 8, respectively, but yield strength and elastic modulus decrease. The precipitation of a high volume fraction of the dendrites (V-dendrite) causes the compositional variation of the dendrites and its counterpart glass matrix. Composition analysis shows that both Hf and Ti elements exhibit an opposite behavior of dissolving into the dendrites during the cooling. About 7-11 at.% component elements (Ti, Cu and Ag) were detected in Ta-rich dendrites, but no Hf element was found. With increasing Vdendrite, the content of component elements dissolving into Ta-rich dendrites decreases from 11.35 at.% for Vdendrite = 4.3% and 7.97 at.% for V-dendrite = 26.5%. Indentation testing was also performed to evaluate the properties of the composites. With increasing Vdendrite, the hardness of the dendrites decreases from 6.0 GPa for x = 3 to 5.21 GPa for x = 12, and its elastic modulus increases from 151.2 GPa for x = 3 to 156.9 GPa for x = 12. The hardness and elastic modulus of the glassy matrix also decrease, respectively, from 9.66 and 148.7 GPa for x = 0 to 9.36 and 137.4 GPa for x = 12 with increasing precipitation of the dendrites. The variation of the properties is due to the compositional change originating from the opposite behavior of Hf and Ti elements to dissolve into the dendrites. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:2037 / 2048
页数:12
相关论文
共 30 条
[1]   In situ formed (CU0.6Zr0.25Ti0.15)93Nb7 bulk metallic glass composites [J].
Bian, Z ;
Ahmad, J ;
Zhang, W ;
Inoue, A .
MATERIALS TRANSACTIONS, 2004, 45 (07) :2346-2350
[2]   Excellent wave absorption by zirconium-based bulk metallic glass composites containing carbon nanotubes [J].
Bian, Z ;
Wang, RJ ;
Pan, MX ;
Zhao, DQ ;
Wang, WH .
ADVANCED MATERIALS, 2003, 15 (7-8) :616-621
[3]   Excellent ultrasonic absorption ability of carbon-nanotube-reinforced bulk metallic glass composites [J].
Bian, Z ;
Wang, RJ ;
Zhao, DQ ;
Pan, MX ;
Wang, ZX ;
Wang, WH .
APPLIED PHYSICS LETTERS, 2003, 82 (17) :2790-2792
[4]   Carbon-nanotube-reinforced Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass composites [J].
Bian, Z ;
Pan, MX ;
Zhang, Y ;
Wang, WH .
APPLIED PHYSICS LETTERS, 2002, 81 (25) :4739-4741
[5]  
BOER FR, 1988, COHESION METALS
[6]   Mechanical properties of Zr57Nb5Al10Cu15.4Ni12.6 metallic glass matrix particulate composites [J].
Conner, RD ;
Choi-Yim, H ;
Johnson, WL .
JOURNAL OF MATERIALS RESEARCH, 1999, 14 (08) :3292-3297
[7]   Melt infiltration casting of bulk metallic-glass matrix composites [J].
Dandliker, RB ;
Conner, RD ;
Johnson, WL .
JOURNAL OF MATERIALS RESEARCH, 1998, 13 (10) :2896-2901
[8]   High-strength Zr-Nb-(Cu,Ni,Al) composites with enhanced plasticity [J].
Das, J ;
Löser, W ;
Kühn, U ;
Eckert, J ;
Roy, SK ;
Schultz, L .
APPLIED PHYSICS LETTERS, 2003, 82 (26) :4690-4692
[9]   Nanostructured composites in multicomponent alloy systems [J].
Eckert, J ;
He, G ;
Das, J ;
Löser, W .
MATERIALS TRANSACTIONS, 2003, 44 (10) :1999-2006
[10]   Al-based nanocrystalline composites by rapid solidification of Al-Ni-Sm alloys [J].
Gloriant, T ;
Greer, AL .
NANOSTRUCTURED MATERIALS, 1998, 10 (03) :389-396