Photoluminescence of La/Ti mixed oxides prepared using sol-gel process and their pCBA photodecomposition

被引：33

作者：

Kim, Hong Rok ^{[1
]}

Lee, Tai Gyu ^{[1
]}

Shul, Yong-Gun ^{[1
]}

机构：

[1] Yonsei Univ, Yonsei Ctr Clean Technol, Seoul 120749, South Korea

来源：

JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY | 2007年 / 185卷 / 2-3期

关键词：

TiO2; photocatalysis; La doping; photoluminescence; pCBA;

D O I：

10.1016/j.jphotochem.2006.05.027

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

La/Ti mixed oxides with weight ratios of 1:9, 2:8, 3:7, and 4:6 were prepared by sol-gel method. The photocatalytic activity of La/Ti oxides was evaluated based on the pCBA photodecomposition. The catalyst samples were characterized by XRD, TEM, DRS, BET, and photoluminescence (PL) spectra. Particles of the La/Ti-mixed oxides showed the diameter of about 7 nm. We found that 30% doping of lanthanum ions on the TiO2 powders induced the highest pCBA (4-chlorobenzonic acid) photodecomposition in these experimental conditions. The order of its photoactivity was as following: 30 > 20 > 0 > 10 > 40 wt%, which was the same for PL tendency. Also, PL spectra intensity increased with calcination temperature from 500 to 600 degrees C, then decreased at 700 degrees C. Phtotcatalytic activity followed the trend of the PL spectra intensity. The modification of TiO2 surface by lanthanum ion made it possible to enhance the photoactivity by retarding the recombination of photoexcited electron/hole pairs, in the result of the higher photoactivity in the stronger PL intensity. (c) 2006 Elsevier B.V. All rights reserved.

引用

页码：156 / 160

页数：5

共 19 条

[11]

LIDE Z, 2001, NANOMATERIALS NANOST, P312

[12] An overview of semiconductor photocatalysis [J].

Mills, A ;

LeHunte, S .

JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 1997, 108 (01) :1-35

[13]

OLLIS DF, 1993, PHOTOCATALYSIS PURIF

[14] Optical properties and X-ray photoelectron spectroscopic study of pure and Pb-doped TiO2 thin films [J].

Rahman, MM ;

Krishna, KM ;

Soga, T ;

Jimbo, T ;

Umeno, M .

JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1999, 60 (02) :201-210

[15] Preparation, characterization, and spectral studies on nanocrystalline anatase TiO2 [J].

Reddy, KM ;

Reddy, CVG ;

Manorama, SV .

JOURNAL OF SOLID STATE CHEMISTRY, 2001, 158 (02) :180-186

[16] Photoacoustic, photoelectrochemical current, and photoluminescence spectra of highly porous, polycrystalline TiO2 electrodes fabricated by chemical synthesis [J].

Toyoda, T ;

Hayakawa, T ;

Shen, Q .

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2000, 78 (2-3) :84-89

[17] The influence of transition metal doping on the physical and photocatalytic properties of titania [J].

Wilke, K ;

Breuer, HD .

JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 1999, 121 (01) :49-53

[18] Photocatalytic decomposition of NO at 275 K on titanium oxide catalysts anchored within zeolite cavities and framework [J].

Yamashita, H ;

Ichihashi, Y ;

Zhang, SG ;

Matsumura, Y ;

Souma, Y ;

Tatsumi, T ;

Anpo, M .

APPLIED SURFACE SCIENCE, 1997, 121 :305-309

[19] Photoluminescence in anatase titanium dioxide nanocrystals [J].

Zhang, WF ;

Zhang, MS ;

Yin, Z ;

Chen, Q .

APPLIED PHYSICS B-LASERS AND OPTICS, 2000, 70 (02) :261-265

← 1 2 →