Analysis of flow-stress measurements of high-purity tungsten single crystals

被引:41
作者
Brunner, D [1 ]
Glebovsky, V
机构
[1] Max Planck Inst Met Forsch, Stuttgart, Germany
[2] Russian Acad Sci, Inst Solid State Phys, Chernogolovka 142432, Russia
基金
俄罗斯基础研究基金会;
关键词
flow-stress measurements; high-purity tungsten; single crystals;
D O I
10.1016/S0167-577X(00)00017-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High-purity W single crystals oriented for single slip were deformed in tension at a constant plastic strain rate between 26 and 800 K. Specimens were isothermally deformed up to their ultimate tensile strain at several temperatures (type-A tests). Another part was deformed successively in small strain intervals at different- decreasing- temperatures (type-B tests) after a first deformation at high temperatures (greater than or equal to 600 K). Tests were combined with stress-relaxation experiments to determine the strain-rate sensitivity of a relevant shear stress. Type-A tests exhibit a parabolic shape of the work-hardening curves with a rather high work-hardening rate at the beginning, which decreases continuously thereafter. In contrast to this behaviour the short stress-strain curves within the shea strain intervals of type-B tests show no work hardening but a plateau after yielding. According to this behaviour a critical resolved shear stress (CRSS) and its strain-rate sensitivity can be determined unambigously. For type-B tests, it turns out that below 775 K, the temperature dependence of the CRSS is non-uniform and exhibits three regimes of different shape. The activation volume and activation enthalpy are determined on the basis that an Arrhenius equation holds for the shear-strain rate. (C) 2000 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:144 / 152
页数:9
相关论文
共 36 条
[21]   ORIENTATION DEPENDENCE OF YIELD IN BODY-CENTERED CUBIC METALS [J].
HULL, D ;
BYRON, JF ;
NOBLE, FW .
CANADIAN JOURNAL OF PHYSICS, 1967, 45 (2P3) :1091-&
[22]   SIZE EFFECT ON ABILITY OF SLIP DEFORMATION IN IRON SINGLE-CRYSTALS AT VERY LOW-TEMPERATURES [J].
KITAJIMA, K ;
AONO, Y ;
ABE, H ;
KURAMOTO, E .
SCRIPTA METALLURGICA, 1979, 13 (11) :1033-1037
[23]  
KOO KC, 1963, ACTA METALL, V11, P1083
[24]  
MYSHLYAEV MM, 1979, PROBL PROCHN, P26
[25]  
Riedle J., 1994, Praktische Metallographie, V31, P580
[26]  
Riedle J, 1996, MATER RES SOC SYMP P, V409, P23
[27]   FRACTURE STUDIES OF TUNGSTEN SINGLE-CRYSTALS [J].
RIEDLE, J ;
GUMBSCH, P ;
FISCHMEISTER, HF ;
GLEBOVSKY, VG ;
SEMENOV, VN .
MATERIALS LETTERS, 1994, 20 (5-6) :311-317
[28]  
ROSE RM, 1962, T METALL SOC AIME, V224, P981
[29]  
SCHADLER HW, 1960, T AM I MIN MET ENG, V218, P649
[30]  
Schubert W. D., 1992, International Journal of Refractory & Hard Metals, V11, P151, DOI 10.1016/0263-4368(92)90057-9