Electrochemical behavior of sintered oxide dispersion strengthened stainless steels

The electrochemical behavior of powder metallurgy (P/M) oxide dispersion strengthened stainless steels (SS) (316L and 434L) have been compared with standard 430 and 316 wrought samples in 0.05 mol/l sulfuric acid. The effects of sintering temperature and yttria addition on the electrochemical behavior have been studied. The behaviour of the dispersion strengthened SS was comparable to that of the straight P/M samples. The straight P/M samples sintered at 1400 degreesC exhibited better corrosion resistance compared to the samples sintered at 1250 degreesC and this has been correlated to sintered densities. The P/M austenitic SS were superior to the P/M ferritic SS. Pitting resistance, studied by cyclic polarization experiments in 3.56 wt.% NaCl, of the P/M samples were comparable to the wrought samples. The addition Of Y2O3 did not affect the pitting resistance. (C) 2003 Elsevier Ltd. All rights reserved.