Toughening with little stiffness loss:: Polyamide filled with ABC triblock copolymers

被引:32
作者
Corte, Laurent
Rebizant, Valery
Hochstetter, Gilles
Tournilhac, Francois
Leibler, Ludwik
机构
[1] Ecole Super Phys & Chim Ind Ville Paris, CNRS, UMR 7167, F-75231 Paris 05, France
[2] CERDATO, F-27470 Arkema, Serquigny, France
关键词
D O I
10.1021/ma061090g
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
In semicrystalline polymers, important toughening is obtained with dispersions of rubber particles. However, adding rubber most often induces a substantial loss in elastic modulus. In the present study, we investigate how to avoid such softening by using ABC triblock copolymers with low rubber content. A polyamide-12 matrix is toughened with polystyrene-block-polybutadiene-block-poly(methyl methacrylate) (SBM) triblock copolymers containing less than 40 wt % of rubber. We compare the mechanical properties of such systems to those of polyamide-12 toughened with pure reactive rubber. Impact properties are characterized by instrumented Charpy testing and post-mortem observations of crack surfaces. We report that dispersions of 10-20 wt % of SBM improve remarkably the impact strength, even at low temperature, without altering the elastic modulus of the polyamide matrix. Microscopic observations suggest that the large differences in impact strength between pure rubber and SBM-filled polyamide arise from differences in particle size and cavitation stress. Three-point bending measurements and dynamic mechanical analysis show that the high modulus of polyamide toughened with SBM is directly related to the low rubber content of the SBM copolymer and that softening also seems to be attenuated by the presence of hard glassy domains of S and M acting as stiffening agents.
引用
收藏
页码:9365 / 9374
页数:10
相关论文
共 46 条
[31]  
MURATOGLU OK, 1995, POLYMER, V36, P4787, DOI 10.1016/00323-8619(59)92945-
[32]  
OOSTENBRINK AJ, 1990, 6 ANN M POL PROC SOC
[33]   The role of matrix molecular weight in rubber toughened nylon 6 blends .3. Ductile-brittle transition temperature [J].
Oshinski, AJ ;
Keskkula, H ;
Paul, DR .
POLYMER, 1996, 37 (22) :4919-4928
[34]   APPLICATION OF INSTRUMENTED IMPACT TEST IN POLYMER TESTING [J].
RADON, JC .
JOURNAL OF APPLIED POLYMER SCIENCE, 1978, 22 (06) :1569-1581
[35]   Chemistry and mechanical properties of epoxy-based thermosets reinforced by reactive and nonreactive SBMX block copolymers [J].
Rebizant, V ;
Venet, AS ;
Tournilhac, F ;
Girard-Reydet, E ;
Navarro, C ;
Pascault, JP ;
Leibler, L .
MACROMOLECULES, 2004, 37 (21) :8017-8027
[36]  
REBIZANT V, 2003, THESIS U P M CURIE P
[37]   IMPACT TESTING OF PLASTICS - PRESENT KNOWLEDGE [J].
SAVADORI, A .
POLYMER TESTING, 1985, 5 (03) :209-241
[38]  
Schrauwen BAG, 2002, MACROMOL SYMP, V185, P89, DOI 10.1002/1521-3900(200208)185:1<89::AID-MASY89>3.0.CO
[39]  
2-I
[40]   INSTRUMENTED IZOD IMPACT TESTING [J].
SLAVIN, SE ;
BESWICK, GT .
JOURNAL OF APPLIED POLYMER SCIENCE, 1993, 49 (06) :1065-1070