Pore size control of carbonized BPDA-pp'ODA polyimide membrane by chemical vapor deposition of carbon

被引：125

作者：

Hayashi, J ^{[1
]}

Mizuta, H ^{[1
]}

Yamamoto, M ^{[1
]}

Kusakabe, K ^{[1
]}

Morooka, S ^{[1
]}

机构：

[1] KYUSHU UNIV,DEPT CHEM SCI & TECHNOL,FUKUOKA 81281,JAPAN

来源：

JOURNAL OF MEMBRANE SCIENCE | 1997年 / 124卷 / 02期

关键词：

pore size; polyimide membrane; chemical vapor deposition;

D O I：

10.1016/S0376-7388(96)00250-5

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

A BPDA-pp'ODA polyimide film was formed on the outer surface of a porous alumina support tube (outside diameter = 2.4 mm), and it was carbonized at an optimized temperature, 700 degrees C. The membrane obtained showed a permeance of 3 x 10(-9) mol . m(-2). s(-1). Pa-1 for O-2 and 2 x 10(-8) mol . m(-2). s(-1). Pa-1 for CO2 and a permselectivity of 10 for O-2/N-2 and 47 for CO2/N-2 at 35 degrees C. The membrane was then modified with carbon deposits formed by pyrolysis of propylene at 650 degrees C. The permselectivities for O-2/N-2 and CO2/N-2 at 35 degrees C were increased to 14 and 73, respectively. Coexisting water vapor decreased permeances of O-2 and N-2 but did not change the O-2/N-2 permselectivity.

引用

页码：243 / 251

页数：9

共 33 条

[11] CHARACTERIZATION OF ULTRAMICROPOROUS CARBON MEMBRANES WITH HUMIDIFIED FEEDS [J].

JONES, CW ;

KOROS, WJ .

INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 1995, 34 (01) :158-163

[12] MOLECULAR-SIEVE CARBON PERMSELECTIVE MEMBRANE .1. PRESENTATION OF A NEW DEVICE FOR GAS-MIXTURE SEPARATION [J].

KORESH, JE ;

SOFER, A .

SEPARATION SCIENCE AND TECHNOLOGY, 1983, 18 (08) :723-734

[13]

KORESH JE, 1986, J CHEM SOC FARAD T 1, V82, P2057, DOI 10.1039/f19868202057

[14]

KOROS WJ, 1995, CHEM ENG PROG, V91, P68

[15] PREPARATION OF SUPPORTED COMPOSITE MEMBRANE BY PYROLYSIS OF POLYCARBOSILANE FOR GAS SEPARATION AT HIGH-TEMPERATURE [J].

KUSAKABE, K ;

LI, ZY ;

MAEDA, H ;

MOROOKA, S .

JOURNAL OF MEMBRANE SCIENCE, 1995, 103 (1-2) :175-180

[16] Morphology and gas permeance of ZSM-5-type zeolite membrane formed on a porous alpha-alumina support tube [J].

Kusakabe, K ;

Yoneshige, S ;

Murata, A ;

Morooka, S .

JOURNAL OF MEMBRANE SCIENCE, 1996, 116 (01) :39-46

[17]

LIDE DR, 1994, CRC HDB THERMOPHYSIC, P81

[18] GAS PERMEATION PROPERTIES OF HEXAFLUORO AROMATIC POLYIMIDES [J].

MATSUMOTO, K ;

XU, P .

JOURNAL OF APPLIED POLYMER SCIENCE, 1993, 47 (11) :1961-1972

[19] THE INFILTRATION OF CARBON-FIBER FELTS AND COMPOSITES BY PYROLYTIC CARBON DEPOSITION FROM PROPYLENE [J].

MCALLISTER, P ;

HENDRICKS, JF ;

WOLF, EE .

CARBON, 1990, 28 (04) :579-588

[20] PRODUCTION OF MOLECULAR-SIEVING CARBON THROUGH CARBONIZATION OF COAL MODIFIED BY ORGANIC ADDITIVES [J].

MIURA, K ;

HAYASHI, J ;

HASHIMOTO, K .

CARBON, 1991, 29 (4-5) :653-660

← 1 2 3 4 →