Dip-coated YBa2Cu3O7-x film by metalorganic deposition using trifluoroacetate

被引：5

作者：

Araki, T

Kurosaki, H

Yuasa, T

Iijima, Y

Saitoh, T

Yamada, Y

Hirabayashi, I

机构：

[1] ISTEC, Superconduct Res Lab, Div 5, Atsuta Ku, Nagoya, Aichi 4568587, Japan

[2] Fujikura Ltd, Mat Technol Lab, Koto Ku, Tokyo 1358512, Japan

来源：

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2002年 / 372卷

关键词：

YBCO; dip coating; metal tape; trifluoroacetate;

D O I：

10.1016/S0921-4534(02)00916-4

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Metalorganic deposition using trifluoroacetates (TFA-MOD) with dip coating was applied for the preparation of YBCO coated conductor, The thickness of the dip-coated films increases with the 0.364th power of the withdrawal speed of substrates. This relationship is common to the case on either single crystal or metal substrate. A 3 cm long dipped YBCO tape on CeO2/YSZ(IBAD)/hastelloy-C is formed at a 5 mm/s withdrawal speed, The tape of 2000 A in thickness has J(c) of 1.0-1.3 MA/cm(2) (77 K, 0 T) measured by the four-probe-method. (C) 2002 Elsevier Science B.V. All rights reserved.

引用

收藏

页码：821 / 824

页数：4

相关论文

共 18 条

[1] Fabrication of YBa2Cu3O7-x films on buffered metal tapes fired at low temperature by MOD method using trifluoroacetate salts [J].

Araki, T ;

Takahashi, Y ;

Yamagiwa, K ;

Yuasa, T ;

Iijima, Y ;

Takeda, K ;

Kim, SB ;

Yamada, Y ;

Hirabayashi, I .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) :2869-2872

[2] Coating processes for YBa2Cu3O7-x superconductor by metalorganic deposition method using trifluoroacetates [J].

Araki, T ;

Kurosaki, H ;

Yamada, Y ;

Hirabayashi, I ;

Shibata, J ;

Hirayama, T .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2001, 14 (09) :783-786

[3] Large-area uniform ultrahigh-Jc YBa2Cu3O7-x film fabricated by the metalorganic deposition method using trifluoroacetates [J].

Araki, T ;

Yamagiwa, K ;

Hirabayashi, I ;

Suzuki, K ;

Tanaka, S .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2001, 14 (07) :L21-L24

[4]

Araki T., 2000, TEION KOGAKU, V35, P516

[5]

ARAKI T, 2001, CERAM T, V112, P293

[6] Thick sol-gel derived YBa2Cu3O7-δ films [J].

Dawley, JT ;

Clem, PG ;

Siegal, MP ;

Overmyer, DL ;

Rodriguez, MA .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) :2873-2876

[7] High Jc YBa2Cu3O7-δ films via rapid, low pO2 pyrolysis [J].

Dawley, JT ;

Clem, PG ;

Siegal, MP ;

Overmyer, DL .

JOURNAL OF MATERIALS RESEARCH, 2001, 16 (01) :13-16

[8] SUPERCONDUCTING OXIDE-FILMS WITH HIGH TRANSITION-TEMPERATURE PREPARED FROM METAL TRIFLUOROACETATE PRECURSORS [J].

GUPTA, A ;

JAGANNATHAN, R ;

COOPER, EI ;

GIESS, EA ;

LANDMAN, JI ;

HUSSEY, BW .

APPLIED PHYSICS LETTERS, 1988, 52 (24) :2077-2079

[9] Growth structure of yttria-stabilized-zirconia films during off-normal ion-beam-assisted deposition [J].

Iijima, Y ;

Hosaka, M ;

Tanabe, N ;

Sadakata, N ;

Saitoh, T ;

Kohno, O ;

Takeda, K .

JOURNAL OF MATERIALS RESEARCH, 1998, 13 (11) :3106-3113

[10] Ion beam assisted growth of fluorite type oxide template films for biaxially textured HTSC coated conductors [J].

Iijima, Y ;

Kakimoto, K ;

Takeda, K .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) :3457-3460