Long lasting phosphorescence of Sr4Al14O25:EU2+,Dy3+ thin films by magnetron sputtering

被引：50

作者：

Chang, CK ^{[1
]}

Mao, DL ^{[1
]}

机构：

[1] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, Shanghai 200030, Peoples R China

来源：

THIN SOLID FILMS | 2004年 / 460卷 / 1-2期

基金：

上海市自然科学基金;

关键词：

sputtering; atomic force microscopy; luminescence; strontium aluminate;

D O I：

10.1016/j.tsf.2004.01.068

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper reports the preparation process and the long lasting phosphorescence of the Sr4Al14O25:Eu2+,Dy3+ thin films obtained by magnetron sputtering. Phosphorescence was achieved by annealing the films in reducing atmosphere. Sr4Al14O25 thin film was obtained when the films were treated at 1200 degreesC, while SrAl2O4 was generated as the intermediate phase during the annealing process. Sr4Al14O25:Eu2+, Dy3+ film generated an emission at 485 nm, and SrAl2O4:Eu2+, Dy3+ film showed an emission peaking at 515 urn. Afterglow characteristics were observed for both films, and Sr4Al14O25:Eu2+, Dy3+ film showed a better afterglow property than the SrAl2O4:Eu2+ ,Dy3+ film due to a deeper trap level and a higher trap concentration formed in the thin films. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：48 / 52

页数：5

共 21 条

[1]

*ASTM, 741810 ASTM

[2]

*ASTM, 740794 ASTM

[3]

BLASSE G, 1968, PHILIPS RES REP, V23, P201

[4] GLOW CURVES WITH GENERAL ORDER KINETICS [J].

CHEN, R .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1969, 116 (09) :1254-&

[5] Thermally stimulated luminescence from x-irradiated porous silicon [J].

Cooke, DW ;

Bennett, BL ;

Farnum, EH ;

Hults, WL ;

Muenchausen, RE ;

Smith, JL .

APPLIED PHYSICS LETTERS, 1997, 70 (26) :3594-3596

[6] Trap states of tris-8-(hydroxyquinoline) aluminum and naphthyl-substituted benzidine derivative using thermally stimulated luminescence [J].

Forsythe, EW ;

Morton, DC ;

Tang, CW ;

Gao, YL .

APPLIED PHYSICS LETTERS, 1998, 73 (11) :1457-1459

[7] Persistent luminescence of Eu2+ doped alkaline earth aluminates, MAl2O4:Eu2+ [J].

Hölsä, J ;

Jungner, H ;

Lastusaari, M ;

Niittykoski, J .

JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 323 :326-330

[8] THERMALLY STIMULATED LUMINESCENCE FROM COMMONLY OCCURRING IMPURITY PHASES IN HIGH-TEMPERATURE SUPERCONDUCTORS [J].

JAHAN, MS ;

COOKE, DW ;

HULTS, WL ;

SMITH, JL ;

BENNETT, BL ;

MAEZ, MA .

JOURNAL OF LUMINESCENCE, 1990, 47 (03) :85-91

[9] Correction of excitation spectra of long persistent phosphors [J].

Jia, DD ;

Zhu, J ;

Wu, BQ .

JOURNAL OF LUMINESCENCE, 2000, 90 (1-2) :33-37

[10] Thermoluminescence properties of SrAl2O4:Eu sputtered films with long phosphorescence [J].

Kato, K ;

Tsutai, I ;

Kamimura, T ;

Kaneko, F ;

Shinbo, K ;

Ohta, M ;

Kawakami, T .

JOURNAL OF LUMINESCENCE, 1999, 82 (03) :213-220

← 1 2 3 →