Effect of HO concentration on TiB2 separation from a self-propagating high-temperature synthesis (SHS) product

被引：34

作者：

Demircan, Umut ^{[1
]}

Derin, Bora ^{[1
]}

Yucel, Onuralp ^{[1
]}

机构：

[1] Tech Univ Istanbul, Met & Mat Engn, TR-34469 Istanbul, Turkey

来源：

MATERIALS RESEARCH BULLETIN | 2007年 / 42卷 / 02期

关键词：

ceramics; chemical synthesis; X-ray diffraction;

D O I：

10.1016/j.materresbull.2006.05.032

中图分类号：

T [工业技术];

学科分类号：

08 [工学];

摘要：

This paper presents a synthesis of TiB2 powder via self-propagating high-temperature synthesis (SHS) method using a mixture of TiO2, B2O3 and Mg followed by acid leaching. In the acid leaching step, the MgO content in the SHS product was leached in different HCl concentrations. X-ray diffraction (XRD) analysis showed that when 9.3 M HCl was used, the leached SHS product was found similar to that of the commercial TiB2 powder. However, scanning electron microscopy (SEM) and BET surface area analysis revealed that the leached product was agglomerated and exhibited very high surface area. (c) 2006 Elsevier Ltd. All rights reserved.

引用

页码：312 / 318

页数：7

共 18 条

[1]

BALE CW, FACTSAGE 5 4 THERMOC

[2]

A facile one-step route to nanocrystalline TiB2 powders [J].

Chen, LY ;

Gu, YL ;

Qian, YT ;

Shi, L ;

Yang, ZH ;

Ma, JH .

MATERIALS RESEARCH BULLETIN, 2004, 39 (4-5) :609-613

[3]

Derin B., 2004, P 10 INT FERR C CAP, P78

[4]

Habashi F., 1997, HDB EXTRACTIVE METAL, P1985

[5]

Effect of NaCl on the synthesis of TiB2 powder by a self-propagating high-temperature synthesis technique [J].

Khanra, AK ;

Pathak, LC ;

Mishra, SK ;

Godkhindi, MM .

MATERIALS LETTERS, 2004, 58 (05) :733-738

[6]

Comparative studies on sintering behavior of self-propagating high-temperature synthesized ultra-fine titanium diboride powder [J].

Khanra, AK ;

Godkhindi, MM ;

Pathak, LC .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (06) :1619-1621

[7]

MUNIR ZA, 1988, CERAM B, V67, P342

[8]

A fast and low-cost room temperature process for TiB2 formation by mechanosynthesis [J].

Ricceri, R ;

Matteazzi, P .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 379 (1-2) :341-346

[9]

Improvement in mechanical properties of in-situ Al-TiB2 composite by incorporation of carbon [J].

Tee, KL ;

Lü, L ;

Lai, MO .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 339 (1-2) :227-231

[10]

Synthesis of in situ Al-TiB2 composites using stir cast route [J].

Tee, KL ;

Lu, L ;

Lai, MO .

COMPOSITE STRUCTURES, 1999, 47 (1-4) :589-593

← 1 2 →