Infrared light absorption of silver film coated on the surface of femtosecond laser microstructured silicon in SF6

被引：18

作者：

Wang, Yulan ^{[1
,2
]}

Liu, Shuying ^{[1
,2
]}

Wang, Yu ^{[3
]}

Feng, Guojin ^{[1
,2
]}

Zhu, Jingtao ^{[1
,2
]}

Zhao, Li ^{[1
,2
]}

机构：

[1] Fudan Univ, Dept Phys, Shanghai 200433, Peoples R China

[2] Fudan Univ, Surface Phys Natl Key Lab, Shanghai 200433, Peoples R China

[3] Natl Inst Metrol, Spectrophotometry Lab, Beijing 100013, Peoples R China

来源：

MATERIALS LETTERS | 2009年 / 63卷 / 30期

关键词：

Microstructure; Optical materials and properties; Silver film; Femtosecond laser pulses; Infrared absorption; Surface plasmon; DANGLING BONDS; ENHANCEMENT;

D O I：

10.1016/j.matlet.2009.09.052

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Absorptive properties of 100 nm thick silver (Ag) films coated on the surface of microstructured silicon prepared by femtosecond laser pulses irradiation in SF6 were measured in a wavelength range of 1.33-16.7 mu m. Greatly enhanced light absorption of Ag films was observed in the entire measured wavelength range. For sample with 6-8 mu m spikes, the absorptance is approximately 0.9 and essentially unchanged in the wavelength region of 1.33-10 mu m, and decreases slightly when lambda>10 mu m. but keeps higher than 0.75 over the whole measured wavelength range. The infrared absorption is strongly related to the height and density of the spikes. While for the samples without Ag coating, the absorption is much lower than that of the Ag films. Multiple reflection of light between spikes and surface plasmon excitation of nano-particles on the spikes surface may lead to the strongly enhanced infrared absorption in such a wide wavelength range. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：2718 / 2720

页数：3

共 25 条

[21]

YAMAGUCHI T, 1974, THIN SOLID FILMS, V21, P173, DOI 10.1016/0040-6090(74)90099-6

[22] Infrared absorption by conical silicon microstructures made in a variety of background gases using femtosecond-laser pulses [J].

Younkin, R ;

Carey, JE ;

Mazur, E ;

Levinson, JA ;

Friend, CM .

JOURNAL OF APPLIED PHYSICS, 2003, 93 (05) :2626-2629

[23]

Zhao M, 2003, CHINESE PHYS LETT, V20, P1789, DOI 10.1088/0256-307X/20/10/338

[24] Enhancement of infrared light absorption of silicon surface-structured by femtosecond laser pulses in N2 ambient [J].

Zhu, Jingtao ;

Zhao, Li ;

Li, Wen ;

Wang, Yu ;

Feng, Guojin ;

Wang, Zhanshan .

MATERIALS LETTERS, 2006, 60 (17-18) :2187-2189

[25]

ZHU JT, 2005, P SOC PHOTO-OPT INS, V276, P5629

← 1 2 3 →