Wet spun chitosan-collagen fibers, their chemical N-modifications, and blood compatibility

Based on an in vitro test for an improvement of the blood compatibility of chitin by blending with tropocollagen, we prepared a novel biocompatible blended fiber and its chemically N-modified fibers. Each (1 g/30 ml) of a clear mixed solution of chitosan with tropocollagen or collagen and a clear solution of chitosan itself in aqueous 2% acetic acid-methanol (2 : 1, v/v) was spun through a viscose-type spinneret into an aqueous 5% ammonia solution containing 40-43% ammonium sulfate at room temperature to afford a white fiber of chitosan-tropocollagen blends (1.08-1.65 g/denier for the tenacity and 10.9-43.2% for the elongation). The tropocollagen content up to 50% by weight) in the blended fiber affected little their tenacity and elongation values. The blended fiber was chemically N-modified at the fiber state by treatment with a series of carboxylic anhydrides and aldehydes to afford the corresponding N-modified fiber (0.86-1.31 g/denier for the tenacity and 8.0-12.1% for the elongation). A transparent blended hydrogel of N-acetylchitosan (chitin) with tropocollagen was produced from the above mixed solution by treatment with acetic anhydride, and its membrane and sponge sheet were also prepared from the hydrogel. (C) 2000 Elsevier Science Ltd. All rights reserved.