Fischer-Tropsch synthesis:: study of the promotion of Pt on the reduction property of Co/Al2O3 catalysts by in situ EXAFS of CoK and Pt LIII edges and XPS

The addition of platinum metal to cobalt/alumina-based Fischer-Tropsch synthesis (FTS) catalysts increases both the reduction rate and, consequently, the density of active cobalt sites. Platinum also lowers the temperature of the two-step conversion of cobalt oxide to cobalt metal observed in temperature programmed reduction (TPR) as Co3O4 to CoO and CoO to Co-0. The interaction of the alumina support with cobalt oxide ultimately determines the active site density of the catalyst surface. This interaction can be controlled by varying the cobalt loading and dispersion, selecting supports with differing surface areas or pore sizes, or changing the noble metal promoter. However, the active site density is observed to depend primarily on the cluster size and extent of reduction, and there is a direct relationship between site density and FTS rate. In this work, in situ extended X-ray absorption ne structure (EXAFS) at the L-m edge of Pt was used to show that isolated Pt atoms interact with supported cobalt clusters without forming observable Pt-Pt bonds. K-edge EXAFS was also used to verify that the cobalt cluster size increases slightly for those systems with Pt promotion. X-ray absorption near-edge spectroscopy (XANES) was used to examine the remaining cobalt clusters after the first stage of TPR, and it revealed that the species were almost entirely cobalt (II) oxide. After the second stage of TPR to form cobalt metal, a residual oxide persists in the sample, and this oxide has been identified as cobalt ( II) aluminate using X-ray photoelectron spectroscopy (XPS). Sequential in situ reduction of promoted and unpromoted systems was also monitored through XPS, and Pt was seen to increase the extent of cobalt reduction by a factor of two.