One-Step Hydrothermal Crystallization of a Layered Double Hydroxide/Alumina Bilayer Film on Aluminum and Its Corrosion Resistance Properties

被引：179

作者：

Guo, Xiaoxiao ^{[1
]}

Xu, Sailong ^{[1
]}

Zhao, Lili ^{[1
]}

Lu, Wei ^{[1
]}

Zhang, Fazhi ^{[1
]}

Evans, David G. ^{[1
]}

Duan, Xue ^{[1
]}

机构：

[1] Beijing Univ Chem Technol, State Key Lab Chem Resource Engn, Beijing 100029, Peoples R China

来源：

LANGMUIR | 2009年 / 25卷 / 17期

基金：

中国国家自然科学基金;

关键词：

HYDROTALCITE CONVERSION COATINGS; SOLVOTHERMAL ION-EXCHANGE; MFI ZEOLITE MEMBRANES; ANION-EXCHANGE; FILIFORM CORROSION; COATED AA2024-T3; AQUEOUS-SOLUTION; THIN-FILMS; AL; ORIENTATION;

D O I：

10.1021/la901012w

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

A zinc-aluminum layered double hydroxide (ZnAl-LDH)/alumina bilayer film has been fabricated on an aluminum substrate by a one-step hydrothermal crystallization method. The LDH film was uniform and compact. XRD patterns and SEM images showed that the LDH film was highly oriented with the c-axis of the crystallites parallel to the substrate surface. The alumina layer existing between the LDH film and the substrate was formed prior to the LDH during the crystallization process. Polarization measurements showed that the bilayer film exhibited a low corrosion current density value of 10(-8) A/cm(2), which means that the LDH/alumina bilayer filth can effectively protect aluminum froth corrosion. Electrochemical impedance spectroscopy (EIS) showed that the impedance of the bilayer was 16 M Omega, meaning that the film served as a passive layer with a high charge transfer resistance. The adhesion between the film and the substrate was very strong which enhances its potential for practical application.

引用

页码：9894 / 9897

页数：4

共 58 条

[1] Highly efficient dye-sensitized solar cells with a titania thin-film electrode composed of a network structure of single-crystal-like TiO2 nanowires made by the "oriented attachment" mechanism [J].

Adachi, M ;

Murata, Y ;

Takao, J ;

Jiu, JT ;

Sakamoto, M ;

Wang, FM .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2004, 126 (45) :14943-14949

[2] A novel glucose sensor based on monodispersed Ni/Al layered double hydroxide and chitosan [J].

Ai, Hanhua ;

Huang, Xintang ;

Zhu, Zhihong ;

Liu, Jinping ;

Chi, Qingbo ;

Li, Yuanyuan ;

Li, Zikun ;

Ji, Xiaoxu .

BIOSENSORS & BIOELECTRONICS, 2008, 24 (04) :1048-1052

[3] Corrosion, erosion and erosion-corrosion performance of plasma electrolytic oxidation (PEO) deposited Al2O3 coatings [J].

Barik, RC ;

Wharton, JA ;

Wood, RJK ;

Stokes, KR ;

Jones, RL .

SURFACE & COATINGS TECHNOLOGY, 2005, 199 (2-3) :158-167

[4] Corrosion resistant high-silica-zeolite MFI coating - One general solution formulation for aluminum alloy AA-2024-T3, AA-5052-H32, AA-6061-T4, and AA-7075-T6 [J].

Beving, Derek E. ;

McDonnell, Andrew M. P. ;

Yang, Weishen ;

Yan, Yushan .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2006, 153 (08) :B325-B329

[5] Heterogeneous ultrathin films fabricated by alternate assembly of exfoliated layered double hydroxides and polyanion [J].

Bin Han, Jing ;

Lu, Jun ;

Wei, Min ;

Wang, Zhong Lin ;

Duan, Xue .

CHEMICAL COMMUNICATIONS, 2008, (41) :5188-5190

[6]

Braterman P.S., 2004, Handbook of layered materials, Ed, P373

[7] Active corrosion protection and corrosion sensing in chromate-free organic coatings [J].

Buchheit, RG ;

Guan, H ;

Mahajanam, S ;

Wong, F .

PROGRESS IN ORGANIC COATINGS, 2003, 47 (3-4) :174-182

[8] In situ microstructure control of oriented layered double hydroxide monolayer films with curved hexagonal crystals as superhydrophobic materials [J].

Chen, Hongyun ;

Zhang, Fazhi ;

Fu, Shanshan ;

Duan, Xue .

ADVANCED MATERIALS, 2006, 18 (23) :3089-+

[9] Direct electrochemistry and electrocatalysis based on a film of horseradish peroxidase intercalated into Ni-Al layered double hydroxide nanosheets [J].

Chen, Xu ;

Fu, Chenglin ;

Wang, Yi ;

Yang, Wensheng ;

Evans, David G. .

BIOSENSORS & BIOELECTRONICS, 2008, 24 (03) :356-361

[10] CORROSION OF ELECTRONIC MATERIALS AND DEVICES [J].

COMIZZOLI, RB ;

FRANKENTHAL, RP ;

MILNER, PC ;

SINCLAIR, JD .

SCIENCE, 1986, 234 (4774) :340-345

← 1 2 3 4 5 6 →