One-Step Hydrothermal Crystallization of a Layered Double Hydroxide/Alumina Bilayer Film on Aluminum and Its Corrosion Resistance Properties

被引：179

作者：

Guo, Xiaoxiao ^{[1
]}

Xu, Sailong ^{[1
]}

Zhao, Lili ^{[1
]}

Lu, Wei ^{[1
]}

Zhang, Fazhi ^{[1
]}

Evans, David G. ^{[1
]}

Duan, Xue ^{[1
]}

机构：

[1] Beijing Univ Chem Technol, State Key Lab Chem Resource Engn, Beijing 100029, Peoples R China

来源：

LANGMUIR | 2009年 / 25卷 / 17期

基金：

中国国家自然科学基金;

关键词：

HYDROTALCITE CONVERSION COATINGS; SOLVOTHERMAL ION-EXCHANGE; MFI ZEOLITE MEMBRANES; ANION-EXCHANGE; FILIFORM CORROSION; COATED AA2024-T3; AQUEOUS-SOLUTION; THIN-FILMS; AL; ORIENTATION;

D O I：

10.1021/la901012w

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

A zinc-aluminum layered double hydroxide (ZnAl-LDH)/alumina bilayer film has been fabricated on an aluminum substrate by a one-step hydrothermal crystallization method. The LDH film was uniform and compact. XRD patterns and SEM images showed that the LDH film was highly oriented with the c-axis of the crystallites parallel to the substrate surface. The alumina layer existing between the LDH film and the substrate was formed prior to the LDH during the crystallization process. Polarization measurements showed that the bilayer film exhibited a low corrosion current density value of 10(-8) A/cm(2), which means that the LDH/alumina bilayer filth can effectively protect aluminum froth corrosion. Electrochemical impedance spectroscopy (EIS) showed that the impedance of the bilayer was 16 M Omega, meaning that the film served as a passive layer with a high charge transfer resistance. The adhesion between the film and the substrate was very strong which enhances its potential for practical application.

引用

页码：9894 / 9897

页数：4

共 58 条

[11] Structural aspects of layered double hydroxides [J].

Evans, DG ;

Slade, RCT .

LAYERED DOUBLE HYDROXIDES, 2006, 119 :1-87

[12] Preparation of layered double hydroxides and their applications as additives in polymers, as precursors to magnetic materials and in biology and medicine [J].

Evans, DG ;

Duan, X .

CHEMICAL COMMUNICATIONS, 2006, (05) :485-496

[13] Applications of layered double hydroxides [J].

Feng, L ;

Duan, X .

LAYERED DOUBLE HYDROXIDES, 2006, 119 :193-223

[14] Surface precipitation of highly porous hydrotalcite-like film on Al from a zinc aqueous solution [J].

Gao, YF ;

Nagai, A ;

Masuda, Y ;

Sato, F ;

Seo, WS ;

Koumoto, K .

LANGMUIR, 2006, 22 (08) :3521-3527

[15]

Gardner E, 2001, ADV MATER, V13, P1263, DOI 10.1002/1521-4095(200108)13:16<1263::AID-ADMA1263>3.0.CO

[16]

2-R

[17] Particle-particle interactions between layered double hydroxide nanoparticles [J].

Gursky, Jennifer A. ;

Blough, Sandra D. ;

Luna, Cesar ;

Gomez, Clarissa ;

Luevano, Amber N. ;

Gardner, Elizabeth A. .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2006, 128 (26) :8376-8377

[18] Preparation of layered double hydroxides [J].

He, J ;

Wei, M ;

Li, B ;

Kang, Y ;

Evans, DG ;

Duan, X .

LAYERED DOUBLE HYDROXIDES, 2006, 119 :89-119

[19] Electrochemical evaluation of a new type of corrosion passivation layer:: Artificially produced Al2O3 films on aluminum [J].

Kuznetsova, A ;

Burleigh, TD ;

Zhukov, V ;

Blachere, J ;

Yates, JT .

LANGMUIR, 1998, 14 (09) :2502-2507

[20] Microstructural optimization of a zeolite membrane for organic vapor separation [J].

Lai, ZP ;

Bonilla, G ;

Diaz, I ;

Nery, JG ;

Sujaoti, K ;

Amat, MA ;

Kokkoli, E ;

Terasaki, O ;

Thompson, RW ;

Tsapatsis, M ;

Vlachos, DG .

SCIENCE, 2003, 300 (5618) :456-460

← 1 2 3 4 5 6 →