Synthesis of an ordered macroporous carbon with 62 nm spherical pores that exhibit unique gas adsorption properties

被引：112

作者：

Kang, S

Yu, JS ^{[1
]}

Kruk, M

Jaroniec, M

机构：

[1] Hannam Univ, Dept Chem, Taejon 306791, South Korea

[2] Kent State Univ, Dept Chem, Kent, OH 44242 USA

来源：

CHEMICAL COMMUNICATIONS | 2002年 / 16期

关键词：

D O I：

10.1039/b204756j

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

An ordered macroporous carbon with 62 nm spherical pores was synthesized using colloidal-crystal templating and found to exhibit unique gas adsorption properties that have been so far attributed to adsorption in mesopores (size below 50 nm).

引用

页码：1670 / 1671

页数：2

共 17 条

[1] STUDIES ON PORE SYSTEMS IN CATALYSTS .11. PORE DISTRIBUTION CALCULATIONS FROM ADSORPTION BRANCH OF A NITROGEN ADSORPTION ISOTHERM IN CASE OF INK-BOTTLE TYPE PORES [J].

BROEKHOFF, JC ;

DEBOER, JH .

JOURNAL OF CATALYSIS, 1968, 10 (02) :153-+

[2]

Egan GL, 2000, ADV MATER, V12, P1040, DOI 10.1002/1521-4095(200007)12:14<1040::AID-ADMA1040>3.0.CO

[3]

2-V

[4] Macroporous carbons prepared by templating silica spheres [J].

Gundiah, G ;

Govindaraj, A ;

Rao, CNR .

MATERIALS RESEARCH BULLETIN, 2001, 36 (09) :1751-1757

[5] Ordered mesoporous polymers of tunable pore size from colloidal silica templates [J].

Johnson, SA ;

Ollivier, PJ ;

Mallouk, TE .

SCIENCE, 1999, 283 (5404) :963-965

[6] Fabrication of novel mesocellular carbon foams with uniform ultralarge mesopores [J].

Lee, J ;

Sohn, K ;

Hyeon, T .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2001, 123 (21) :5146-5147

[7] Fabrication of well-ordered macroporous active carbon with a microporous framework [J].

Lei, ZB ;

Zhang, YG ;

Wang, H ;

Ke, YX ;

Li, JM ;

Li, FQ ;

Xing, JY .

JOURNAL OF MATERIALS CHEMISTRY, 2001, 11 (08) :1975-1977

[8] Colloidal imprinting: A novel approach to the synthesis of mesoporous carbons [J].

Li, ZJ ;

Jaroniec, M .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2001, 123 (37) :9208-9209

[9] Preparation of a high surface area microporous carbon having the structural regularity of Y zeolite [J].

Ma, ZX ;

Kyotani, T ;

Tomita, A .

CHEMICAL COMMUNICATIONS, 2000, (23) :2365-2366

[10] PREPARATION OF SIO2 NANOPARTICLES IN A NONIONIC REVERSE MICELLAR SYSTEM [J].

OSSEOASARE, K ;

ARRIAGADA, FJ .

COLLOIDS AND SURFACES, 1990, 50 (50) :321-339

← 1 2 →